Chinese Journal of Catalysis p. 1142 - 1154 (2015)
Update date:2022-08-16
Topics:
Yuan, Ye
Wang, Zhimiao
An, Hualiang
Xue, Wei
Wang, Yanji
CeO2 nanotubes (CeO2-NT) were synthesized using carbon nanotubes as template by a liquid phase deposition and hydrothermal method. X-ray diffraction, transmission electron microscopy, and N2 adsorption-desorption were used to characterize the CeO2-NT. The wall of CeO2-NT was composed of small interconnected nanocrystallites ranging from 4 to 9 nm in size. The specific surface area of CeO2-NT was 108.8 m2/g with an outer diameter of 25 nm and length > 300 nm. Supported Pd catalyst, Pd-O/CeO2-NT, was prepared using CeO2-NT as the support. Temperature-programmed reduction analysis showed that the surface oxygen on Pd-O/CeO2-NT could be reduced at low temperature, therefore it showed high activity in the reaction. Pd-O/CeO2-NT was used as the catalyst for the oxidative carbonylation of phenol. It has better activity and DPC selectivity than Pd-O/CeO2-P, which was prepared by supporting Pd on zero dimensional CeO2 particles. Under the optimized conditions, phenol conversion was 67.7% with 93.3% DPC selectivity with Pd-O/CeO2-NT. However, its catalytic activity decreased when the catalyst was used for the second time. This was attributed to the destruction of the tubular structure of Pd-O/CeO2-NT and Pd leaching during the reaction.
View MoreChangzhou Ruiping Chemical Co., Ltd
website:http://www.wishchem.com
Contact:+86-519-82324280
Address:No.288-1 Huacheng Road, Jintan
Shandong Jiulong Hisince Pharmaceutical Co.,Ltd.
Contact:+86-15853188990
Address:Huadian Pioneer Park, Huadian Township, Qihe County, Dezhou City, Shandong, P.R.China
Contact:+ 86 512 52491118
Address:1 Fuyu Road, Haiyu TownChangshu, Jiangsu, China
Contact:(1) 206-3550089
Address:5115 NE 8TH PL, Renton, WA 98059 USA
WUXI KINGHAN BIO-MEDICAL&CHEMICAL INC.
Contact:13861062998
Address:Room 1316,No.1619 Huishan Avenue,Wuxi,China
Doi:10.1080/00397911.2018.1537398
(2019)Doi:10.1002/anie.202013474
(2021)Doi:10.1021/j150642a033
(1983)Doi:10.1016/S0040-4039(00)90011-X
(1965)Doi:10.1016/j.molstruc.2016.09.005
(2017)Doi:10.1007/BF02290751
(1997)