1. with high transparency, no discoloration, good self-adhesive, good retraction ratio, good tensile properties, 1 meter can be on 3-5 meters use.
2. non-toxic, tear-resistant, anti-puncture, hot temperature endurable;
3. water-proof, moisture-proof, dust-proof, anti-corrosion
4. this is pallet wrap film(lldpe stretch film) produced by three layer common extruding machine, it provide excellent protection for the surface of packed products. it can reduce packaging cost, its economical, labor saving, efficiency increasing. its easy to use and remove, suitable for palletized packaging of products and transportation
linear low density polyethylene (lldpe)
production of linear low density polyethylene to ethylene as the main raw material, 1 - butene or 1 - hexene as comonomer, the catalyst for the gas fluidized bed polymerization. reaction out of material by granulation, drying, and sent packing.
performance of linear low density polyethylene non-toxic, tasteless, odorless white particles, density of 0.918 ~ 0.935g/cm3. compared with ldpe, and the higher softening temperature and melting temperature, there is strength, toughness, rigidity, heat, cold and good, but also has good resistance to environmental stress cracking resistance, impact strength, resistance tear strength properties. and can be acid, alkali, organic solvents.
use for the production of plastic sheeting, packaging films, laminated films, tubes, hollow containers, wire, cable insulation layer.
lldpe film grade
tests | value | unit |
melt flow rate (mfr) | 2.0±0.4 | g/10min |
density | 920±2 | kg/cm3 |
tensile strengthat yield | 8 | mpa ≥ |
tensile strengthat break | 12 | mpa ≥ |
haze | 15 | %≤ |
lldpe for master batch use
tests | value | unit |
melt flow rate (mfr) | 20 | g/10min |
density | 0.924 | g/cm3 |
tensile strength | md12 | mpa |
td 10 | ||
elongation at yield | 13 | % |
elongation at break | 200 | |
dark drop impact | 105 | g |
brittle temperature(f 50) | -70 | °c |
vicat softening point | 90 | °c |
lldpe powder rotational molding grade for tank use
tests | value | unit |
melt flow rate (mfr) | 3.2 | g/10min |
density | 0.939 | g/cm3 |
melting point | 127 | °c |
tensile yield strength | 21 | mpa |
tensile strength at break | 28 | mpa |
elongation at break | 1,100 | % |
flexural modulus | 750 | mpa |
brittle temperature | <-60 | °c |