Cupric oxide (cas 1317-38-0)-based p-type Transparent Conductors☆
-
Add time:08/20/2019 Source:sciencedirect.com
This study examines the impact of doping on the resistivity of sputtered cupric oxide (CuO), and investigates the effects of co-sputtering CuO with tin dioxide (SnO2). It was found that films sputtered from a 2 at. % sodium-doped target have resistivities of four orders of magnitude lower than equivalent undoped films. Addition of oxygen was found to reduce the resistivity further. The best films were found to have resistivities of 4.3x10-2 Ω.cm. Co-sputtering with SnO2 was found to increase the band gap significantly, although it also caused an increase in the resistivity. All mixed oxide films were both amorphous and p-type.
We also recommend Trading Suppliers and Manufacturers of Cupric oxide (cas 1317-38-0). Pls Click Website Link as below: cas 1317-38-0 suppliers
Prev:Biosynthesis of nano Cupric oxide (cas 1317-38-0) on cotton using Seidlitzia rosmarinus ashes utilizing bio, photo, acid sensing and leaching properties
Next:A cleaner route for nanocolouration of wool fabric via green assembling of Cupric oxide (cas 1317-38-0) nanoparticles along with antibacterial and UV protection properties) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Electrochemical behaviour and voltammetric determination of mercury (II) ion in Cupric oxide (cas 1317-38-0)/poly vinyl alcohol nanocomposite modified glassy carbon electrode08/23/2019
- Comparison of experimental and calculated thermophysical properties of alumina/Cupric oxide (cas 1317-38-0) hybrid nanofluids08/22/2019
- A cleaner route for nanocolouration of wool fabric via green assembling of Cupric oxide (cas 1317-38-0) nanoparticles along with antibacterial and UV protection properties08/21/2019
- Biosynthesis of nano Cupric oxide (cas 1317-38-0) on cotton using Seidlitzia rosmarinus ashes utilizing bio, photo, acid sensing and leaching properties08/19/2019
- Fabrication of a semi-transparent flexible humidity sensor using kinetically sprayed Cupric oxide (cas 1317-38-0) film08/18/2019
- Stimulated low frequency Raman scattering in Cupric oxide (cas 1317-38-0) nanoparticles water suspension08/17/2019
- The role of cupric ions in the oxidative dissolution process of marmatite: A dependence on Cu2+ concentration08/16/2019
- Evaluation of hybrid anion exchanger containing Cupric oxide (cas 1317-38-0) for As(III) removal from water08/15/2019
-
Health and Chemical more >