Synthesis of large plate-like gypsum dihydrate from waste gypsum board
-
Add time:09/08/2019 Source:sciencedirect.com
This paper reports the synthesis of large plate-like gypsum (calcium sulfate) dihydrate generated from waste gypsum board via a wet process. Gypsum hemihydrate was formed by dehydrating waste gypsum board in a sodium sulfate solution at 100 °C for 1 h to form needle-like crystals. The large gypsum dihydrate was formed by lowering the temperature of the gypsum hemihydrate suspension below 80 °C. The large plate-like gypsum dihydrate was obtained by adding seed crystals to a suspension cooled at 80 °C. When 40 μm seed crystals were added at 0.5 mass%, the large plate-like gypsum dihydrate crystals obtained from waste gypsum board had average dimensions of 250 μm length × 100 μm width × 35 μm thickness.
We also recommend Trading Suppliers and Manufacturers of Magnesium nitrate dihydrate. (cas 15750-45-5). Pls Click Website Link as below: cas 15750-45-5 suppliers
Prev:On the catalysis of calcium oxalate dihydrate formation by osteopontin peptides
Next:Effect of Ca(II) on the multistep kinetic behavior of thermally induced oxidative decomposition of cerium(III) oxalate to CeO2(IV)) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- On the catalysis of calcium oxalate dihydrate formation by osteopontin peptides09/07/2019
- Materials Science CommunicationEffect of magnesium on the crystallization and the microhardness of dicalcium phosphate dihydrate09/06/2019
- One-pot hydrothermal synthesis, in vitro biodegradation and biocompatibility of Sr-doped nanorod/nanowire hydroxyapatite coatings on ZK60 magnesium alloy09/05/2019
-
Health and Chemical more >