New Journal of Chemistry p. 5873 - 5883 (2020)
Update date:2022-08-30
Topics:
Ferri
Campisi
Carniti
Gervasini
Shen
A mesoporous carbon (CMC) has been treated under acidic conditions (32.5 wt% HNO3 at 10 °C or 40 °C) to prepare two new carbon samples (HCMC10 and HCMC40), which developed higher acidity in terms of quantity of sites and surface acid strength. The properties of the three carbons have been studied by using various techniques (N2 adsorption/desorption, TEM, XRPD, Raman spectroscopy, 13C NMR, 2D 1H-13C NMR, and XPS). Aromatic -COOH and -OH groups were identified as the main surface acid sites. Acid site density has been determined by pulse liquid-solid phase adsorption experiments carried out in different liquids. The samples retained acidity features in water, due to hydrophobicity of the surfaces, while acidity dropped when measured in methanol. From NH3-TPD analysis, a ranking of acid strength could be obtained: HCMC40 > HCMC10 > CMC. The good acidity of the carbon samples allowed them to act as catalysts in the hydrolysis reaction of sucrose to glucose and fructose. The catalytic activity of the carbon samples was compared to that of Amberlite, a commercial sulfated acid resin; the observed kinetic constant of HCMC40 was similar to that of Amberlite.
View MoreSHAANXI FUJIE PHARMACEUTICAL CO.,LTD
website:http://www.fujiepharm.com
Contact:+86-29-63650906
Address:Yuanqu Yi Road, Qinghe Food Industrial Park, Sanyuan County, Shaanxi Province, China
Contact:+86-579-85206992
Address:No 451 chouzhou north road ,room 1106 int'l business center , yiwu ,china
Shanghai Forever Biotech Co., Ltd.
Contact:+86-21-69734790
Address:Room 5017/5019、5022、5024 of Technology Innovation Centre, No.1155, Gongyuan East Rd, QingPu District, Shanghai China.
Contact:86 21 3772 9386
Address:Rm.1803,Starry Bldg.1,1505 Meijiabang Road,Shanghai 201620 China
Weifang Dongxing Chitosan Factory
website:http://dxchitosan.lookchem.com/
Contact:13475651157
Address:Weifang city ,shandong province
Doi:10.1248/cpb.16.17
(1968)Doi:10.1081/NCN-120022607
(2003)Doi:10.1021/acs.joc.8b01668
(2018)Doi:10.1021/jm400480j
(2013)Doi:10.1039/b416699j
(2005)Doi:10.1021/np000593r
(2001)