504-03-0Relevant articles and documents
Low-CTE photosensitive polyimide based on semialicyclic poly(amic acid) and photobase generator
Ogura, Tomohito,Higashihara, Tomoya,Ueda, Mitsuru
, p. 1317 - 1323 (2010)
A negative-type photosensitive polyimide (PSPI) based on semialicyclic poly(amic acid) (PAA), poly( frans-1, 4-cyclohexylenediphenylene amic acid), and {[(4, 5-dimethoxy-2-nitrobenzyl)oxy]carbonyl]} 2, 6-dimethylpiperidlne (DNCDP) as a photobase generator has been developed as a next-generation buffer coat material. The semialicyclic PAA was synthesized from 3, 3', 4, 4'-biphenyltetracarboxylic dianhydride and frans1, 4-cyclohexyldiamine in the presence of acetic acid, and the PAA polymerization solution was directly used for PSPI formulation. This PSPI, consisting of PAA (80 wt %) and DNCDP (20 wt %), showed high sensitivity of 70 mJ/cm2 and high contrast of 10.3, when it was exposed to a 365-nm line (i-line), postexposure baked at 190 °C for 5 min, and developed with 2, 38 wt % tetramethylammonium hydroxide aqueous solution containing 20 wt % isopropanol at 25 °C. A clear negative image of 6-μm line and space pattern was printed on a film, which was exposed to 500 mJ/cm2 of i-line by a contact printing mode and fully converted to poly(trans-1, 4-cyclohexylenebiphenylene imide) pattern upon heating at 250 °C for 1 h. The PSPI film had a low coefficient of thermal expansion of 16 ppm/K compared to typical PIs, such as prepared from 3, 3', 4, 4'-biphenyltetracarboxylic dianhyariae ana 4, 4'-oxydianiline
Hydrogenation of N-Heteroarenes Using Rhodium Precatalysts: Reductive Elimination Leads to Formation of Multimetallic Clusters
Kim, Sangmin,Loose, Florian,Bezdek, Máté J.,Wang, Xiaoping,Chirik, Paul J.
, p. 17900 - 17908 (2019/11/19)
A rhodium-catalyzed method for the hydrogenation of N-heteroarenes is described. A diverse array of unsubstituted N-heteroarenes including pyridine, pyrrole, and pyrazine, traditionally challenging substrates for hydrogenation, were successfully hydrogenated using the organometallic precatalysts, [(η5-C5Me5)Rh(N-C)H] (N-C = 2-phenylpyridinyl (ppy) or benzo[h]quinolinyl (bq)). In addition, the hydrogenation of polyaromatic N-heteroarenes exhibited uncommon chemoselectivity. Studies into catalyst activation revealed that photochemical or thermal activation of [(η5-C5Me5)Rh(bq)H] induced C(sp2)-H reductive elimination and generated the bimetallic complex, [(η5-C5Me5)Rh(μ2,η2-bq)Rh(η5-C5Me5)H]. In the presence of H2, both of the [(η5-C5Me5)Rh(N-C)H] precursors and [(η5-C5Me5)Rh(μ2,η2-bq)Rh(η5-C5Me5)H] converted to a pentametallic rhodium hydride cluster, [(η5-C5Me5)4Rh5H7], the structure of which was established by NMR spectroscopy, X-ray diffraction, and neutron diffraction. Kinetic studies on pyridine hydrogenation were conducted with each of the isolated rhodium complexes to identify catalytically relevant species. The data are most consistent with hydrogenation catalysis prompted by an unobserved multimetallic cluster with formation of [(η5-C5Me5)4Rh5H7] serving as a deactivation pathway.
Titanium(III)-Oxo Clusters in a Metal-Organic Framework Support Single-Site Co(II)-Hydride Catalysts for Arene Hydrogenation
Ji, Pengfei,Song, Yang,Drake, Tasha,Veroneau, Samuel S.,Lin, Zekai,Pan, Xiandao,Lin, Wenbin
, p. 433 - 440 (2018/01/17)
Titania (TiO2) is widely used in the chemical industry as an efficacious catalyst support, benefiting from its unique strong metal-support interaction. Many proposals have been made to rationalize this effect at the macroscopic level, yet the underlying molecular mechanism is not understood due to the presence of multiple catalytic species on the TiO2 surface. This challenge can be addressed with metal-organic frameworks (MOFs) featuring well-defined metal oxo/hydroxo clusters for supporting single-site catalysts. Herein we report that the Ti8(μ2-O)8(μ2-OH)4 node of the Ti-BDC MOF (MIL-125) provides a single-site model of the classical TiO2 support to enable CoII-hydride-catalyzed arene hydrogenation. The catalytic activity of the supported CoII-hydride is strongly dependent on the reduction of the Ti-oxo cluster, definitively proving the pivotal role of TiIII in the performance of the supported catalyst. This work thus provides a molecularly precise model of Ti-oxo clusters for understating the strong metal-support interaction of TiO2-supported heterogeneous catalysts.