Effect of Ag substitution on structural, magnetic and magnetocaloric properties of Pr0.6Sr0.4–xAgxMnO3 manganites

Add time:08/02/2019    Source:sciencedirect.com

A systematic investigation on the structural, magnetic and magnetocaloric properties of Pr0.6Sr0.4–xAgxMnO3 (x=0.05 and 0.1) manganites was reported. Rietveld refinements of the X-ray diffraction patterns confirmed that all samples were single phase and crystallized in the orthorhombic structure with Pnma space group. Magnetic measurements in a magnetic applied field of 0.01 T revealed that the ferromagnetic-paramagnetic transition temperature TC decreased from about 293 to 290 K with increasing silver content from x=0.05 to 0.1. The reported magnetocaloric entropy change and relative cooling power for both samples were considerably remarkable with a ΔSmax value of 1.9 J/(kg·K) and maximum RCP values of 100 J/kg, under a magnetic field change (Δµ0H) equal to 1.8 T. The analysis of the universal curves gave an evidence of a second order magnetic transition for the studied samples. The magnetic field influence on both the magnetic entropy change and the relative cooling power was also studied and discussed.

We also recommend Trading Suppliers and Manufacturers of LITHIUM MANGANITE (cas 12163-00-7). Pls Click Website Link as below: cas 12163-00-7 suppliers

Prev:Influence of sodium doping on the electrical and magnetic properties of La0.90Li0.10MnO3 manganites
Next:Chemically modified Ba6Mn24O48 tunnel manganite as a lithium insertion host)