60083-50-3Relevant articles and documents
Hydrogen absorption in the Zr-Al system
Clark, N. J.,Wu, E.
, p. 227 - 244 (1990)
A series of Zr-Al alloys has been prepared and the reaction with hydrogen studied by microbalance thermogravimetric analysis and differential thermal analysis. Their geometric and electronic structures have been studied by X-ray powder diffraction, X-ray
Phase equilibria in the ternary Al-Zr-La system
Peng, Dan,Zhan, Yongzhong,She, Jia,Pang, Mingjun,Du, Yong
, p. 62 - 66 (2011/01/09)
The phase relationships in the Al-Zr-La ternary system at 773 K have been investigated for the first time mainly by means of X-ray powder diffraction (XRD) and scanning electron microscopy (SEM) equipped with energy dispersive analysis (EDX). The existenc
HIGH-TEMPERATURE OXIDATION OF ZrAl.
Paljevic M.
, p. 107 - 112 (2008/10/08)
The oxidation of ZrAl in dry oxygen in the temperature range 800 - 1100 K follows a parabolic rate law. An activation energy of 86. 4 kJ mol** minus **1 was estimated. During the oxidation, aluminum diffuses from the oxide layer to the ZrAl bulk, thus forming a ZrAl//2 phase very close to the oxide-alloy interface. The excess zirconium is therefore selectively oxidized, yielding tetragonal mainly and monoclinic ZrO//2 containing no Al//2O//3.