A fluorine-containing sulfonyl imide volute season ammonium salt electrolyte, its preparation and use (by machine translation)
-
Paragraph 0040-0041, (2019/01/08)
The invention discloses a fluorine-containing sulfonyl imide volute season ammonium salt electrolyte, has the following structure: Wherein n is 1 or 2; Y- For N (SO2 F)2 - Or N (SO2 CF3 )2 - , N (SO2 C2 F5 )2 - , N (SO2 F) (SO2 CF3 )- , N (SO2 OCH2 CF3 )2 - In a. The invention also discloses the fluorine-containing sulfonyl imide volute season ammonium salt electrolyte preparation method and for use in the super capacitor electrolyte. The invention fluorine-containing sulfonyl imide volute season ammonium salt electrolyte has excellent performance, is used in the super capacitor electrolyte in the ultra-low temperature (- 40 °C) under the extreme conditions demonstrate the excellent electrochemical performance; preparation method of this invention in accordance with the demand of environmental protection. (by machine translation)
Inorganic salt templated porous TiO2 photoelectrode for solid-state dye-sensitized solar cells
Li, Hao,Li, Shichao,Zhang, Ye,Yan, Feng
, p. 346 - 352 (2016/01/09)
TiO2 photoelectrodes with channels (or pores) are prepared by using an inorganic salt (NaHCO3) as a template. NaHCO3 doped TiO2 slurries deposited on a compacted TiO2 film are heated at 150 °C, which releases CO2 gas and water vapour, thus forming channels (or pores) inside a TiO2 light-scattering photoelectrode. These channels (pores) improve the penetration degree of solid-state electrolytes into the TiO2 photoelectrode and enhance the photovoltaic efficiency of resulting DSSCs (dye sensitized solar cells). With a channel (pore) size of ~500 nm diameter, an ionic liquid plastic crystal, 5-azoniaspiro[4.4]nonane bis(trifluoromethanesulfonyl)imide (N44TFSI), shows power conversion efficiencies of 6.1% and 5.4% under 1.5 solar spectrum illuminations at 50 and 100 mW cm-2, respectively.
Method for synthesizing spiro quartenary ammonium systems
-
Page/Page column 6; 10, (2010/11/26)
A method for preparing a spiro quaternary ammonium system and electrolytes containing spiro quaternary ammonium cations, comprising a synthesizing step wherein a spiro ammonium system is formed in a medium that can serve as both the reaction solvent and as an electrolyte solvent.