Stabilization of the thermodynamically favored polymorph of cadmium chalcogenide nanoparticles CdX (X = S, Se, Te) in the polar mesopores of SBA-15 silica
Yosef, Maekele,Schaper, Andreas K.,Froeba, Michael,Schlecht, Sabine
, p. 5890 - 5896 (2005)
A versatile synthetic approach to cadmium chalcogenide nanoparticles in the mesopores of SBA-15 silica as a host matrix was developed. The use of cadmium organochalcogenolates of the type Cd(XPh)2·TMEDA (X = S, Se, Te) allowed the preparation of nanoparticles of all three cadmium chalcogenides following the same experimental protocol. Particles of CdS, CdSe, and CdTe with a particle size of 7 nm were prepared from this class of single-source precursors. The incorporation of the precursor molecules into the pores was achieved by melt infiltration at a temperature of 140°C. Subsequent pyrolysis of the precursors in the mesopores yielded the semiconductor particles. Owing to the high polarity of the silanol-covered pore walls, which lower the surface energy of the particles to a large extent, the dimorphic cadmium chalcogenides are obtained in their thermodynamically favored modifications; e.g., CdS particles crystallize in the wurtzite type, CdTe particles are obtained in the zinc blende structure, and CdSe (where no unambiguous preference exists) crystallizes as a mixture of both structures with a rather random stacking sequence.