Organic template-free synthesis of zeolite Y nanoparticle assemblies and their application in the catalysis of the Ritter reaction
Tang, Ting,Zhang, Lei,Dong, Hai,Fang, Zhongxue,Fu, Wenqian,Yu, Quanyong,Tang, Tiandi
, p. 7711 - 7717 (2017/02/05)
Zeolite Y nanoparticle assemblies (Y-NA) with a mesoporous structure were directly synthesized at 75?°C for 16 h without adding any organic templates. The changes in structure, morphology and textural parameters of the materials obtained after different crystallization times were investigated via powder X-ray diffraction (XRD), infrared spectroscopy (IR), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and N2-sorption. The results show that Y-NA had a micro-mesoporous structure composed of highly crystalline particle assemblies with sizes of 400-900 nm. The H-form Y-NA (HY-NA) is strongly acidic, and exhibits a good catalytic performance in the Ritter reaction, as compared with the H-form microporous zeolite Y and mesoporous zeolite ZSM-5.
An efficient and scalable ritter reaction for the synthesis of t-butyl amides
Milne, Jacqueline E.,Baum, Jean C.
, p. 519 - 526 (2014/04/17)
-
An efficient method for the conversion of aromatic and aliphatic nitriles to the corresponding N-tert-butyl amides: A modified Ritter reaction
Reddy, K. Laxma
, p. 1453 - 1455 (2007/10/03)
Aromatic and aliphatic nitriles react with tert-butyl acetate in the presence of a catalytic amount of sulfuric acid to give the corresponding N-tert-butyl amides in excellent yields.