Constrained geometry titanium complexes: Exceptionally robust systems for living polymerization of methacrylates at high temperature and model studies toward chain transfer polymerization with thiols
Lian, Bing,Thomas, Christophe M.,Navarro, Christophe,Carpentier, Jean-Francois
, p. 187 - 195 (2008/10/09)
The 1:1 combination of Ti{CGC}Me2 (1; CGC = Me 2Si(Me4C5)(tBuN)) with B(C6F 5)3 was found to feature a so far unrevealed thermal robustness in methacrylate polymerization that enables it to operate in a broad temperature range (0-100°C) with a living behavior. Highly effective (576 kg PMMA·mol Ti-1·h-1) and productive (monomer-to-Ti ratio up to 5000) homopolymerization of methyl methacrylate (MMA) and effective diblock and triblock copolymerization of MMA with butyl methacrylate (BMA) were thus achieved at 80°C. The robust constrained geometry titanium system has been used to investigate thiols as possible chain transfer agents in MMA polymerization. Neutral alkylthiolato and thiophenolato complexes [Ti{CGC}(X)(Y)] (2, X = Me, Y = tBuS; 3, X = Me, Y = o-MeOC6H4S; 4, X = Y = iPrS; 5, X = Y = PhCH2S) have been synthesized by protonolysis of 1 with thiols and shown to polymerize MMA once activated by a Lewis acid such as B(C6F5) 3. Combinations 1/B(C6F5)3/tBuSH polymerized quantitatively MMA in toluene to yield PMMAs with narrow polydispersity (Mw/Mn ?1 .10), but no effective chain transfer was evidenced, whatever the conditions used. The stoichiometric reaction of tBuSH and o-MeOC6H4SH with the cationic enolate complex [Ti{CGC}(O(OiPr)C=CMe2)-(THF)]+[MeB(C 6F5)3]- (8) revealed that thiols do cleave the Ti-O(enolate) bond of 8 to give the alkylthiolato and thiophenolato titanium cationic species; however, this pathway proceeds remarkably slowly in comparison with that with a similar Zr-O(enolate) bond.