Chemical hydrophobisation of silica-based porous particles with N-OCTADECYLTRICHLOROSILANE (cas 112-04-9) (ODTCS) by a solventless process in a fluidised-bed reactor
-
Add time:08/20/2019 Source:sciencedirect.com
This study describes a new technique for hydrophobisation of silica powders in a fluidised fluidised-bed reactor. The hydrophobisation treatment is based on silanisation reaction of silica with N-OCTADECYLTRICHLOROSILANE (cas 112-04-9) (ODTCS). However, contrary to conventional silanisation processes, the reaction is performed at dry phase by mixing two classes of particles during the fluidisation: “target particles” to be treated (a fine microporous silica powder) and “ODTCS-carrier” particles consisting of coarser porous alumina beads containing an adequate amount of reagent. The results showed that the silanisation reagent was successfully anchored on silica surface and achieved high surface coverage (1.4 groups/nm2) in only few minutes. The energy consumption is reduced if the reaction is carried out at low temperatures but using humidified air (7% RH). These conditions promote however a vertical polymerization of the reagent on solids surface. However, an optimum temperature exists as, for example, the reaction at 80 °C with 7% RH gave a relatively interesting hydrophobic powder.
We also recommend Trading Suppliers and Manufacturers of N-OCTADECYLTRICHLOROSILANE (cas 112-04-9). Pls Click Website Link as below: cas 112-04-9 suppliers
Prev:Fluorimetric determination of hydrogen peroxide by use of the fluorescence reaction between N-(4′-hydroxyphenyl)-N-(4-methylquinolinyl)amine and cobalt(II) in the presence of Trimethylstearylammonium Chloride (cas 112-03-8)☆
Next:Formation mechanism of N-OCTADECYLTRICHLOROSILANE (cas 112-04-9) monolayer prepared at the air/water interface) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Preparation and characterization of asymmetric planar supported bilayers composed of poly(bis-sorbylphosphatidylcholine) on N-OCTADECYLTRICHLOROSILANE (cas 112-04-9) SAMs08/24/2019
- Significantly improved stability of N-OCTADECYLTRICHLOROSILANE (cas 112-04-9) self-assembled monolayer by plasma pretreatment on mica08/23/2019
- Hot-embossing performance of silicon micromold coated with self-assembled N-OCTADECYLTRICHLOROSILANE (cas 112-04-9)08/22/2019
- Formation mechanism of N-OCTADECYLTRICHLOROSILANE (cas 112-04-9) monolayer prepared at the air/water interface08/21/2019