Relevant academic research and scientific papers

Selective synthesis of epichlorohydrin: Via liquid-phase allyl chloride epoxidation over a modified Ti-MWW zeolite in a continuous slurry bed reactor

The epoxidation of allyl chloride (ALC) to epichlorohydrin (ECH) with H2O2 using a piperidine (PI)-modified Ti-MWW catalyst (Ti-MWW-PI) in a continuous slurry reactor was investigated to develop an efficient reaction system for the corresponding industrial process. The reaction parameters, including solvent, reaction temperature, t-butanol/ALC mass ratio, ALC/H2O2 molar ratio, weight hourly space velocity of H2O2, and the addition amount of ammonia, were studied in detail to pursue high H2O2 conversion and ECH selectivity. A long catalytic lifetime of 244 h was achieved at high H2O2 conversion (>97.0%) and ECH selectivity (>99.8%) under optimized reaction conditions. The crystallinity was well maintained for the deactivated Ti-MWW-PI catalyst, which was regenerated by a combination of calcination and piperidine treatment. This journal is

Readily Scalable Methodology for the Synthesis of Nonsymmetric Glyceryl Diethers by a Tandem Acid-/Base-Catalyzed Process

A useful optimized synthetic methodology has been designed for the synthesis of nonsymmetric glyceryl diethers from epichlorohydrin. A tandem process combining a cheap, heterogeneous, and fully recoverable acid catalyst and alkaline hydroxide is used for the synthesis of a variety of glycerol-derived ethers bearing different alkyl substituents in 1 and 3 positions. Different heterogeneous acid catalysts have been tested for the reaction of epichlorohydrin with several alcohols, the best results being obtained with readily available recoverable and inexpensive montmorillonite-K10 and Nafion NR50. For the second reaction step, potassium hydroxide is used. In all the cases, good yields of the desired glyceryl diethers are obtained in smooth reaction conditions, always with total conversion of epichlorohydrin and without the need of intermediate purification. Scale-up of the tandem process has been carried out with good results.

Epoxide ring opening with alcohols using heterogeneous Lewis acid catalysts: Regioselectivity and mechanism

Lewis acidic catalytic materials are investigated for the regioselective ring opening of epoxides with alcohols. For ring opening epichlorohydrin with methanol, the catalytic activity shows a strong dependence on the type of support and Lewis acidic species used. While Sn-SBA-15 is catalytically active, significantly higher catalytic activity can be achieved with hydrothermally synthesized zeolites of which Sn-Beta is 6 and 7 times more active than Zr-Beta or Hf-Beta, respectively. Sn-Beta is determined to be more active and more regioselective for epoxide ring opening of epichlorohydrin with methanol than Al-Beta. For Sn-Beta, the activation energy for the reaction between epichlorohydrin and methanol is determined to be 53 ± 7 kJ mol?1. For epichlorohydrin, the activation energy barrier and experimentally observed regioselectivity are found using DFT to be consistent with a concerted reaction mechanism involving activation of the epoxide on an alcohol adsorbed on the catalytic site and nucleophilic attack by a second alcohol. The epoxide is shown to impact the regioselectivity and the mechanism since isobutylene oxide is selectively ring opened by methanol to form the terminal alcohol. DFT calculations indicate the mechanism for isobutylene ring opening involves epoxide activation and ring opening on an alcohol adsorbed onto the catalytic site. Finally, catalyst reuse testing indicates that Sn-Beta can be used for multiple reactions with no decrease in activity and limited to no leaching of the tin site, demonstrating Sn-Beta is a promising catalytic material for epoxide ring opening reactions with alcohols.

Zirconium triflate grafted on SBA-15 as a highly efficient solid acid catalyst for ring opening of epoxides by amines and alcohols

Metal (Al, Ti, Zr) triflate grafted mesoporous SBA-15 (AlTf/S, TiTf/S, ZrTf/S) samples were synthesized as inexpensive solid acid materials by a simple one-pot-two-step synthesis methodology. These materials were characterized by X-ray diffraction, N2-sorption, thermogravimetric analysis, Fourier transform infrared spectroscopy (FT-IR), in-situ pyridine FT-IR spectroscopy, and elemental analysis. ZrTf/S was found to be a highly efficient and reusable solid acid catalyst for ring opening of epoxides with amines and alcohols and produced β-amino alcohols and β-alkoxy alcohols respectively under ambient reaction conditions. The ZrTf/S catalyst showed the highest activity, which was attributed to its high acidity compared with that of the Ti and Al containing samples.

Enhancement of CO2 Adsorption and Catalytic Properties by Fe-Doping of [Ga2(OH)2(L)] (H4L = Biphenyl-3,3′,5,5′-tetracarboxylic Acid), MFM-300(Ga2)

Metal-organic frameworks (MOFs) are usually synthesized using a single type of metal ion, and MOFs containing mixtures of different metal ions are of great interest and represent a methodology to enhance and tune materials properties. We report the synthesis of [Ga2(OH)2(L)] (H4L = biphenyl-3,3′,5,5′-tetracarboxylic acid), designated as MFM-300(Ga2), (MFM = Manchester Framework Material replacing NOTT designation), by solvothermal reaction of Ga(NO3)3 and H4L in a mixture of DMF, THF, and water containing HCl for 3 days. MFM-300(Ga2) crystallizes in the tetragonal space group I4122, a = b = 15.0174(7) ? and c = 11.9111(11) ? and is isostructural with the Al(III) analogue MFM-300(Al2) with pores decorated with -OH groups bridging Ga(III) centers. The isostructural Fe-doped material [Ga1.87Fe0.13(OH)2(L)], MFM-300(Ga1.87Fe0.13), can be prepared under similar conditions to MFM-300(Ga2) via reaction of a homogeneous mixture of Fe(NO3)3 and Ga(NO3)3 with biphenyl-3,3′,5,5′-tetracarboxylic acid. An Fe(III)-based material [Fe3O1.5(OH)(HL)(L)0.5(H2O)3.5], MFM-310(Fe), was synthesized with Fe(NO3)3 and the same ligand via hydrothermal methods. [MFM-310(Fe)] crystallizes in the orthorhombic space group Pmn21 with a = 10.560(4) ?, b = 19.451(8) ?, and c = 11.773(5) ? and incorporates μ3-oxo-centered trinuclear iron cluster nodes connected by ligands to give a 3D nonporous framework that has a different structure to the MFM-300 series. Thus, Fe-doping can be used to monitor the effects of the heteroatom center within a parent Ga(III) framework without the requirement of synthesizing the isostructural Fe(III) analogue [Fe2(OH)2(L)], MFM-300(Fe2), which we have thus far been unable to prepare. Fe-doping of MFM-300(Ga2) affords positive effects on gas adsorption capacities, particularly for CO2 adsorption, whereby MFM-300(Ga1.87Fe0.13) shows a 49% enhancement of CO2 adsorption capacity in comparison to the homometallic parent material. We thus report herein the highest CO2 uptake (2.86 mmol g-1 at 273 K at 1 bar) for a Ga-based MOF. The single-crystal X-ray structures of MFM-300(Ga2)-solv, MFM-300(Ga2), MFM-300(Ga2)·2.35CO2, MFM-300(Ga1.87Fe0.13)-solv, MFM-300(Ga1.87Fe0.13), and MFM-300(Ga1.87Fe0.13)·2.0CO2 have been determined. Most notably, in situ single-crystal diffraction studies of gas-loaded materials have revealed that Fe-doping has a significant impact on the molecular details for CO2 binding in the pore, with the bridging M-OH hydroxyl groups being preferred binding sites for CO2 within these framework materials. In situ synchrotron IR spectroscopic measurements on CO2 binding with respect to the -OH groups in the pore are consistent with the above structural analyses. In addition, we found that, compared to MFM-300(Ga2), Fe-doped MFM-300(Ga1.87Fe0.13) shows improved catalytic properties for the ring-opening reaction of styrene oxide, but similar activity for the room-temperature acetylation of benzaldehyde by methanol. The role of Fe-doping in these systems is discussed as a mechanism for enhancing porosity and the structural integrity of the parent material.

MIL-101-SO3H: A highly efficient Bronsted acid catalyst for heterogeneous alcoholysis of epoxides under ambient conditions

For the first time, a ～100% sulfonic acid functionalized metal-organic framework (MOF), MIL-101-SO3H, with giant pores has been prepared by a hydrothermal process followed by a facile postsynthetic HCl treatment strategy. The replete readily accessible Lewis acidic and especially Bronsted acidic sites distributed throughout the framework as well as high stability endow the resultant MOF exceptionally high efficiency and recyclability, which surpass all other MOF-based catalysts, for the ring opening of epoxides with alcohols (especially, methanol) as nucleophiles under ambient conditions.

Opening of Cyclic Acetals by Trichloro-, Dichloro- and Tribromo-borane

The rate-determining step in the ring opening of cyclic acetals by trichloroborane to yield α-chloro-ethers is shown to be consistent with the formation of an oxocarbenium ion.Subsequent reduction provides a general route for the conversion of a diol into a hydroxy-ether.Tribromoborane is a more powerful and dichloroborane a less powerful reagent than trichloroborane.