Angewandte Chemie International Edition
10.1002/anie.201809702
COMMUNICATION
toluene under inert atmosphere and refluxed for 3 days. In a short time
period (1-2 h) the precipitate of polymer started to appear in the reaction
flask. After completion of the reaction the precipitate was filtered and
washed with hot toluene, DMF, chloroform, THF and methanol (3 times
each solvent). Subsequently the Soxhlet extraction was performed using
chloroform, THF and methanol (24 h each solvent). Afterwards the solid
was dried in the vacuum drying oven at 120 oC for 24 h. More detailed
reaction parameters can be found in Table S2.
[12] K. Kailasam, M. B. Mesch, L. Möhlmann, M. Baar, S. Blechert, M.
Schwarze, M. Schröder, R. Schomäcker, J. Senker, A. Thomas, Energy
Technol. 2016, 4, 744-750.
[13] a) U. Salzner, J. Phys. Chem. B 2002, 106, 9214-9220; b) M. Keshtov,
D. Godovsky, V. Kochurov, G. D. Sharma, F.-C. Chen, N. Radychev, A.
Khokhlov, AIP Conference Proceedings 2014, 1599, 498-501.
[14] K. Schwinghammer, B. Tuffy, M. B. Mesch, E. Wirnhier, C. Martineau, F.
Taulelle, W. Schnick, J. Senker, B. V. Lotsch, Angew. Chem. Int. Ed.
2013, 52, 2435-2439.
[
15] a) D. Schwarz, Y. Noda, J. Klouda, K. Schwarzová-Pecková, J. Tarábek,
J. Rybáček, J. Janoušek, F. Simon, M. V. Opanasenko, J. Čejka, A.
Acharjya, J. Schmidt, S. Selve, V. Reiter-Scherer, N. Severin, J. P. Rabe,
P. Ecorchard, J. He, M. Polozij, P. Nachtigall, M. J. Bojdys, Adv. Mater.
2017, 29, 1703399-n/a; b) S. Kuecken, A. Acharjya, L. Zhi, M. Schwarze,
R. Schomacker, A. Thomas, Chem. Commun. 2017, 53, 5854-5857.
16] M.-S. Kim, C. S. Phang, Y. K. Jeong, J. K. Park, Polym. Chem. 2017, 8,
Acknowledgements
We thank Mária Piatková, Martina Rimmele and André Sanches
for upscaling and help with fluorescence measurements, Barbora
[
[
[
2
Balcarova for N sorption measurements, Stanislava Matějková
5
655-5659.
17] P. Kuhn, M. Antonietti, A. Thomas, Angew. Chem. Int. Ed. 2008, 47,
450-3453.
for ICP-OES, Adam Málek for IR spectroscopy measurements,
Martin Dračínský for access to solid-state NMR facilities, and Dr.
Miroslav Štěpánek for solid-state fluorescence measurements.
A.A., J.S. and A.T. acknowledge support from the German
Science Foundation (Project TH1463/15-1) and the Cluster of
Excellence (UniCat). M.J.B. thanks the European Research
Council (ERC) for funding under the Starting Grant Scheme
3
18] M. Valamanesh, C. Langlois, D. Alloyeau, E. Lacaze, C. Ricolleau,
Ultramicroscopy 2011, 111, 149-154.
[19] K. S. W. Sing, D. H. Everett, R. A. W. Haul, L. Moscou, R. A. Pierotti, J.
Rouquerol, T. Siemieniewska, Pure Appl. Chem. 1985, 57, 603-619.
[
[
20] S. Ren, M. J. Bojdys, R. Dawson, A. Laybourn, Y. Z. Khimyak, D. J.
Adams, A. I. Cooper, Adv. Mater. 2012, 24, 2357-2361.
(
BEGMAT-678462).
21] a) S. Ren, R. Dawson, D. J. Adams, A. I. Cooper, Polym. Chem. 2013,
4, 5585-5590; b) H. Bohra, S. Y. Tan, J. Shao, C. Yang, A. Efrem, Y.
Keywords: conjugated microporous polymers • donor-acceptor
systems • fluorescence sensing • photocatalysis • triazine
Zhao, M. Wang, Polym. Chem. 2016, 7, 6413-6421; c) Y. Liao, J. Weber,
B. M. Mills, Z. Ren, C. F. J. Faul, Macromolecules 2016, 49, 6322-6333.
22] a) X. Liu, Y. Xu, D. Jiang, J. Am. Chem. Soc. 2012, 134, 8738-8741; b)
S. Gu, J. Guo, Q. Huang, J. He, Y. Fu, G. Kuang, C. Pan, G. Yu,
Macromolecules 2017, 50, 8512-8520.
[
[
[
[
1]
2]
3]
F. K. Kessler, Y. Zheng, D. Schwarz, C. Merschjann, W. Schnick, X.
Wang, M. J. Bojdys, Nat. Rev. Mat. 2017, 2, 17030.
[
[
[
23] J.-K. Chen, S.-M. Yang, B.-H. Li, C.-H. Lin, S. Lee, Langmuir 2018, 34,
P. Guiglion, C. Butchosa, M. A. Zwijnenburg, Macromol. Chem. Phys.
1441-1446.
2
016, 217, 344-353.
a) J.-X. Jiang, A. Trewin, D. J. Adams, A. I. Cooper, Chem. Sci. 2011, 2,
777-1781; b) D. Schwarz, Y. S. Kochergin, A. Acharjya, A. Ichangi, M.
24] L. Li, Z. Cai, Q. Wu, W.-Y. Lo, N. Zhang, L. X. Chen, L. Yu, J. Am. Chem.
Soc. 2016, 138, 7681-7686.
1
25] D. Schwarz, A. Acharja, A. Ichangi, P. Lyu, V. Opanasenko Maksym, R.
Goßler Fabian, A. F. König Tobias, J. Čejka, P. Nachtigall, A. Thomas,
J. Bojdys Michael, Chem. - Eur. J. 2018
V. Opanasenko, J. Čejka, U. Lappan, P. Arki, J. He, J. Schmidt, P.
Nachtigall, A. Thomas, J. Tarábek, M. J. Bojdys, Chem. - Eur. J. 2017,
23, 13023-13027.
[
4]
a) J. Roncali, Macromol. Rapid Commun. 2007, 28, 1761-1775; b) R. S.
Sprick, J.-X. Jiang, B. Bonillo, S. Ren, T. Ratvijitvech, P. Guiglion, M. A.
Zwijnenburg, D. J. Adams, A. I. Cooper, J. Am. Chem. Soc. 2015, 137,
3265-3270.
[
[
5]
6]
J.-X. Jiang, F. Su, A. Trewin, C. D. Wood, N. L. Campbell, H. Niu, C.
Dickinson, A. Y. Ganin, M. J. Rosseinsky, Y. Z. Khimyak, A. I. Cooper,
Angew. Chem. Int. Ed. 2007, 46, 8574-8578.
C. Gu, Y. Chen, Z. Zhang, S. Xue, S. Sun, K. Zhang, C. Zhong, H. Zhang,
Y. Pan, Y. Lv, Y. Yang, F. Li, S. Zhang, F. Huang, Y. Ma, Adv. Mater.
2013, 25, 3443-3448.
[
[
7]
8]
R. S. Sprick, B. Bonillo, M. Sachs, R. Clowes, J. R. Durrant, D. J. Adams,
A. I. Cooper, Chem. Commun. 2016, 52, 10008-10011.
W. Huang, J. Byun, I. Rörich, C. Ramanan, P. W. M. Blom, H. Lu, D.
Wang, L. C. d. Silva, R. Li, LeiWang, K. Landfester, K. A. I. Zhang, Angew.
Chem. Int. Ed. 2018, 57, 8316-8320.
[
[
[
9]
E. E. Havinga, W. ten Hoeve, H. Wynberg, Polymer Bulletin 1992, 29,
119-126; b) C. R. Chenthamarakshan, J. Eldo, A. Ajayaghosh,
Macromolecules 1999, 32, 251-257.
10] a) M. Belletête, J.-F. Morin, S. Beaupré, M. Ranger, M. Leclerc, G.
Durocher, Macromolecules 2001, 34, 2288-2297; b) S. A. Jenekhe, L. Lu,
M. M. Alam, Macromolecules 2001, 34, 7315-7324.
11] a) M. Held, Y. Zakharko, M. Wang, F. Jakubka, F. Gannott, J. W. Rumer,
R. S. Ashraf, I. McCulloch, J. Zaumseil, Org. Electron. 2016, 32, 220-
227; b) A. Facchetti, Mater. Today 2013, 16, 123-132.
This article is protected by copyright. All rights reserved.