Passivating film artificially built on LiNi0.5Mn1.5O4 by molecular layer deposition of (pentafluorophenylpropyl)Trimethoxysilane (cas 2487-90-3)

Add time:07/11/2019    Source:sciencedirect.com

In this study, (pentafluorophenylpropyl)trimethoxysilane (PFPPS) is grafted on a nickel-doped manganese spinel (LiNi0.5Mn1.5O4, LNMO) surface to suppress the failure modes in the 5-V positive electrode; electrolyte oxidation/film deposition, acid generation, and metal (Ni and Mn) dissolution. Vapor-phase molecular layer deposition is used to deposit a uniformly covered PFPPS layer on the LNMO surface. When the Li/LNMO cell is cycled at 3.5–4.9 V (vs. Li/Li+), the PFPPS moiety on the LNMO surface remains intact (not oxidized) under the highly oxidizing condition. Several beneficial features are observed with the PFPPS grafting. The oxidative electrolyte decomposition is mitigated, which increases the Coulombic efficiency of the Li/LNMO cell. Consequently, the surface film deposition and cell polarization are reduced, improving the capacity retention. Moreover, the acid generation and metal dissolution are also mitigated.

We also recommend Trading Suppliers and Manufacturers of Trimethoxysilane (cas 2487-90-3). Pls Click Website Link as below: cas 2487-90-3 suppliers

Prev:Application of functionalized nano HMS type mesoporous silica with N-(2-aminoethyl)-3-aminopropyl Methyldimethoxysilane (cas 16881-77-9) as a suitable adsorbent for removal of Pb (II) from aqueous media and industrial wastewater
Next:Multilayer-tuned surface plasmon modes using molecular nanolayer of (3-mercaptopropyl)Trimethoxysilane (cas 2487-90-3) applicable for nanobiosensing application)