Growth of Cu2S thin films by atomic layer deposition using Cu(dmamb)2 and H2S

Add time:07/19/2019    Source:sciencedirect.com

In this study, atomic layer deposition (ALD) of Cu2S was explored using bis(dimethylamino-2-methyl-2-butoxy)copper(II) and 5% H2S combination as Cu and S sources, respectively. The reaction resulted in a high growth rate of ∼0.22–0.24 nm/cycle at 150–200 °C owing to the high reactivity of the Cu precursor. At all investigated temperatures, Cu2S films with Cu oxidation state of +1 were obtained with negligible impurity levels. It was revealed that stoichiometric Cu2S films could be deposited at 120–150 °C, while sulfur deficient films was formed at 200 °C. Cu2S ALD process at low temperatures of 100–120 °C resulted in continuous film formation while the higher deposition temperatures of >150 °C led to island formation. Cu2S films showed p-type electrical characteristic with high hole concentrations of 4 × 1019–1021 cm−3 and Hall mobility of 2 cm2/vs. Lastly, the as-deposited Cu2S films exhibited an optical band gap of 1.2 eV which widened upon prolonged surface oxidation and in addition displayed NIR intra-band absorption.

We also recommend Trading Suppliers and Manufacturers of (S)-4-(2-METHYL-BUTOXY)-PHENYLAMINE (cas 112418-54-9). Pls Click Website Link as below: cas 112418-54-9 suppliers

Prev:Biochemical mechanisms conferring cross-resistance between Tebufenozide (cas 112410-23-8) and abamectin in Plutella xylostella
Next:Unconventional Knoevenagel-type indoles: Synthesis and cell-based studies for the identification of pro-apoptotic agents)