Enhanced fatigue properties of nanostructured austenitic SUS 316L (cas 11134-23-9) stainless steel
-
Add time:07/20/2019 Source:sciencedirect.com
The present communication reports on the substantial improvement in monotonic and cyclic strength of austenitic 316L stainless steel nanostructured during equal channel angular pressing (ECAP). The ultimate tensile strength and the fatigue limit after ECAP exceed 1.3 GPa and 550 MPa, respectively, while the ductility was not fully compromised. Microstructural observations showed that these excellent mechanical properties can be attributed to the nanostructure created due to intensive twinning, with an inter-twin spacing of 30–40 nm.
We also recommend Trading Suppliers and Manufacturers of SUS 316L (cas 11134-23-9). Pls Click Website Link as below: cas 11134-23-9 suppliers
Prev:Effect of cold work on the irradiation creep of SUS 316L (cas 11134-23-9)
Next:Influence of macro segregation on hydrogen environment embrittlement of SUS 316L (cas 11134-23-9) stainless steel) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Influence of filler metals and welding techniques on the structure–property relationships of Inconel 718 and AISI 316L dissimilar weldments07/29/2019
- Small Punch Creep deformation and rupture behavior of 316L(N) stainless steel07/28/2019
- Giga-cycle Fatigue of AISI 316L After Sensitising of Structure07/27/2019
- Investigation on un-peened and laser shock peened dissimilar weldments of Inconel 600 and AISI 316L fabricated using activated-TIG welding technique07/26/2019
- Keyhole gas tungsten arc welding of AISI 316L stainless steel07/25/2019
- Antibacterial 316L Stainless Steel Containing Silver and Niobium07/24/2019
- Measurement methods for surface oxides on SUS 316L (cas 11134-23-9) in simulated light water reactor coolant environments using synchrotron XRD and XRF07/23/2019
- Influence of macro segregation on hydrogen environment embrittlement of SUS 316L (cas 11134-23-9) stainless steel07/22/2019
- Effect of cold work on the irradiation creep of SUS 316L (cas 11134-23-9)07/21/2019