Solution-processed ternary alloy aluminum yttrium oxide dielectric for high performance indium zinc oxide thin-film transistors

Add time:07/20/2019    Source:sciencedirect.com

In this study, we evaluated the structural, chemical, and electrical properties of ternary alloy aluminum yttrium oxide (Al2-xYxO3) films prepared by employing a low-cost spin-cast technique. Al2-xYxO3 films annealed at 400 °C were found to possess smooth and excellent insulating characteristics compared to their binary Al2O3 or Y2O3 film counterparts. This superior performance of the Al2-xYxO3 films as a gate insulator can be explained based on structure stabilization from the cation alloying mixing effect. The amorphous indium zinc oxide (a-IZO) thin-film transistor (TFT) with the ternary alloy Al0.45Y1.55O3 film exhibited a high mobility of 52.9 cm2/V, a low subthreshold gate swing of 0.19 V/decade, a threshold voltage of −0.51 V, a high ION/OFF ratio of 4 × 106, and good hysteresis-free stability, suggesting that the solution-based Al0.45Y1.55O3 dielectric film is an attractive candidate as a gate dielectric for high-performance and low-cost a-IZO TFTs.

We also recommend Trading Suppliers and Manufacturers of YTTRIUM ALUMINUM OXIDE (cas 12005-21-9). Pls Click Website Link as below: cas 12005-21-9 suppliers

Prev:Variation of Eu3+ emissions in YTTRIUM ALUMINUM OXIDE (cas 12005-21-9)s controlled by amount of La3+ dopant
Next:Broadband down-conversion in Bi3+–Yb3+-codoped yttrium and yttrium–aluminum oxides)