Effect of corrosion methods on morphology of superparamagnetic and flexible iron oxide nanobrushes

Add time:07/29/2019    Source:sciencedirect.com

Superparamagnetic iron oxide nanobrushes with different morphologies prepared using an anodic aluminum oxide Template (AAO) template. Flexible polymers and the precursor iron oxide nanoparticles coated with polyacrylic acid (PAA) were assembled into iron oxide nanobrushes. The iron oxide nanobrushes with different morphologies were obtained by etching the alumina template with different degrees. The morphologies of the iron oxide nanobrush arrays were characterized with field emission scanning electron microscope (FESEM). The hysteresis loops of the iron oxide nanobrush arrays were measured using vibrating sample magnetometry (VSM), where the coercivity and remanence are almost zero, to achieve a typical superparamagnetism. The contact angle test shows that the iron oxide nanobrushes have hydrophilicity. These superparamagnetic and flexible iron oxide nanobrushes might be used in self-cleaning surfaces and sensors driven by a magnetic field.

We also recommend Trading Suppliers and Manufacturers of phosphoric acid, aluminium iron salt (cas 19034-12-9). Pls Click Website Link as below: cas 19034-12-9 suppliers

Prev:Effects of acidic concentrations, temperatures and nitrates on the solubility of K2SiF6 in phosphoric acid and nitric acid solutions
Next:Influence of aluminum ions distribution on the removal of aluminum from rare earth solutions using saponified naphthenic acid)