Flame-retardant thermoplastic polyester based on multiarm aluminum phosphinate for improving anti-dripping

Add time:07/31/2019    Source:sciencedirect.com

A novel multiarm aluminum salt of pentaerythrityl ester of tetra(carboxyethylmethylphosphinic acid) (Alcpp) was synthesized and added into thermoplastic polyester elastomer (TPEE). Thermal analysis, evolved gas analysis (TGA-FTIR), flammability tests (LOI, UL94), microcombustion calorimeter (MCC) and chemical analyses of residues (SEM-EDX) were used. Alcpp provides TPEE with desired flame retardancy and anti-dripping property and shows a good compatibility with TPEE. TGA-FTIR and SEM-EDX analysis show that Alcpp can depress the heating release and promote the char forming and acts mainly in condensed phase. In addition, Alcpp combining with MPP achieves better fire-resistant performance than Alcpp alone. When total additives is kept 28 wt%, 25 wt% Alcpp combining 3 wt% MPP exhibits the optimum synergy by increasing char yield and depressing heat release and flammability. The reason for the synergy is due to a strong compact carbonaceous char resulting from reaction between Alcpp and MPP, which effectively prevent the dripping of the TPEE during combustion.

We also recommend Trading Suppliers and Manufacturers of Zinc phosphinate (cas 15060-64-7). Pls Click Website Link as below: cas 15060-64-7 suppliers

Prev:Flame retardancy mechanisms of aluminium phosphinate in combination with melamine polyphosphate and zinc borate in glass-fibre reinforced polyamide 6,6
Next:Fluorescence sensing response of zinc(II) and pyrophosphate ions by benzoxazole appended dipodal Schiff base)