Preparation of reusable glass hollow fiber membranes and methylene blue adsorption

Add time:07/23/2019    Source:sciencedirect.com

In this work, the PVDF/glass as-prepared composite membrane was prepared through phase-inversion method and used to adsorb methylene blue dye. The results of SEM and BET showed that the membrane had an asymmetric nanoscale porous structure. The electronegativity on the surface of membrane was determined through zeta potential test. The adsorption properties of as-prepared composite membrane and glass membrane were studied through testing the removal ratio of methylene blue from aqueous solution. Then the effects of membranes dose, pH value, temperature and initial concentration on the removal ratio were systematically studied. The adsorption mechanism was also studied. The adsorption kinetics and adsorption isotherm fitted well with the pseudo-second-order model and Freundlich model, respectively. In addition, the adsorption efficiency of glass membrane basically remained 85% after eight repeated adsorption-calcination cycles. The obtained membranes could be reused for methylene blue removal with high efficiency for multiply times.

We also recommend Trading Suppliers and Manufacturers of Solvent Blue 94 (cas 123515-19-5). Pls Click Website Link as below: cas 123515-19-5 suppliers

Prev:Sugaring-out extraction of 2,3-Butanediol (cas 123513-85-9) from fermentation broths
Next:Improving biocatalysis of cefaclor with penicillin acylase immobilized on magnetic nanocrystalline cellulose in deep eutectic solvent based co-solvent)