Evolution of pressure-amorphized Zirconium tungstate (cas 16853-74-0) upon annealing

Add time:07/31/2019    Source:sciencedirect.com

Zirconium tungstate (cas 16853-74-0) Zr(WO4)2 exhibits irreversible amorphization at high pressure. Upon heating, the pressure-amorphized phase transforms into different phase/phases depending on the pressure applied during heating. Transformation of pressure-amorphized samples to metastable cubic phase during isochronal annealing at ambient pressure is investigated using X-ray diffraction and Raman spectroscopy. Though the X-ray diffraction and Raman spectra show only monotonic changes up to 850 K in the amorphous state, the sample exhibits dramatic changes in the color from gray to black to white. The relaxation of the amorphous phase during annealing suggests gradual irreversible volume increase by about 6%, whereas the tungstate tetrahedra are found to shrink. Crystallization to cubic phase at 900 K is accompanied by a large increase in the sample volume. The specific volumes of the amorphous phases obtained from cycling the samples to different pressures suggest the possibility of polyamorphism in this system.

We also recommend Trading Suppliers and Manufacturers of Zirconium tungstate (cas 16853-74-0). Pls Click Website Link as below: cas 16853-74-0 suppliers

Prev:Facial synthesis, characterization of graphene oxide-Zirconium tungstate (cas 16853-74-0) (GO-Zr(WO4)2) nanocomposite and its application as modified microsensor for dopamine
Next:Preparation and characterization of zirconium silico188W-tungstate as a base material for 188W/188Re generator)