On the self-propagating high-temperature synthesis of TUNGSTEN BORIDE (cas 12007-09-9) containing composite powders from WO3–B2O3–Mg system

Add time:07/24/2019    Source:sciencedirect.com

In this research, the self-propagating high-temperature synthesis characteristics of the 2WO3‒(1 + x)B2O3‒(9 + y)Mg system were studied using H3BO3 as the boron oxide source. The addition of extra B2O3 and Mg was considered as the main process parameter to obtain TUNGSTEN BORIDE (cas 12007-09-9)s phases. XRD results showed that tungsten element was the only phase remained after leaching of the products obtained with the stoichiometric composition. The extra B2O3 and Mg acted as the diluent agents and decreased the adiabatic temperature and the reaction velocity as well as the products’ particle size. Moreover, tungsten boride containing composite powders were obtained. However, the type of the tungsten boride in the composites was dependent on the diluent agent. Fourier transformed infrared spectroscopy analysis showed that nearly-pure composite powders were obtained after acid leaching. Finally, based on the XRD phase analysis and differential thermal analysis results, a mechanism was suggested for the formation of the SHS products in this system.

We also recommend Trading Suppliers and Manufacturers of TUNGSTEN BORIDE (cas 12007-09-9). Pls Click Website Link as below: cas 12007-09-9 suppliers

Prev:High-performance, low-cost titanium metal matrix composites
Next:Toxicogenomic responses of human alveolar epithelial cells to TUNGSTEN BORIDE (cas 12007-09-9) nanoparticles)