Effect of nano-size oxy-nitride starting precursors on spark plasma sintering of calcium sialons along the alpha/(alpha + beta) phase boundary
-
Add time:07/29/2019 Source:sciencedirect.com
Several compositions of calcium stabilized sialon ceramics were synthesized by using nano-size starting powder precursors and spark plasma sintering technique at a relatively low temperature of 1500 °C. The formation of calcium alpha/beta-sialons was investigated for the compositions represented by Cam/2Si12-(m+n)Alm+nOnN16-n where m and n values were varied from 0.6 to 1.6 and 0.4–1.6, respectively. Phase analysis of the selected compositions helped in developing the phase boundary between alpha and alpha/beta phase regimes. Effect of m and n values on the evolution of the final phase(s), densification and mechanical properties were evaluated. All samples yielded densified ceramics with density values (3.13–3.19 g/cm3) comparable with those reported in the literature for similar compositions and synthesized at temperatures greater than 1700 °C via conventional sintering techniques. Vickers hardness value HV10 of 20 GPa was measured for the Ca0.5Si10.6Al1.4O0.4N15.6 composition (with m = 1.0 and n = 0.4) synthesized at 1500 °C. An increase in n value (higher oxide content) was observed to facilitate the formation of beta-sialon and AlN polytype phases leading to an increase in fracture toughness but a decrease in Vickers hardness.
We also recommend Trading Suppliers and Manufacturers of CALCIUM NITRIDE (cas 12013-82-0). Pls Click Website Link as below: cas 12013-82-0 suppliers
Prev:Low-temperature spark plasma sintering of calcium stabilized alpha sialon using nano-size aluminum nitride precursor
Next:Highly efficient of molybdenum trioxide-cadmium titanate nanocomposites for ultraviolet light photocatalytic and antimicrobial application: Influence of reactive oxygen species) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Low-temperature spark plasma sintering of calcium stabilized alpha sialon using nano-size aluminum nitride precursor07/28/2019
- The synthesis and structure of new transition metal lithium CALCIUM NITRIDE (cas 12013-82-0) compounds07/27/2019
- Enhancement of the graphitic carbon nitride surface properties from calcium salts as templates07/26/2019
- In situ reactive multi-material Ti6Al4V-calcium phosphate-nitride coatings for bio-tribological applications07/25/2019
- Experimental investigation on thermodynamic and kinetic of calcium hydroxide dehydration with hexagonal boron nitride doping for thermochemical energy storage07/24/2019
-
Health and Chemical more >
-
Related Products
- Calcium valproate
- Calcium (1)-bis(2-hydroxy-4-methylvalerate)
- Calcium (2S)-2-[(4-chlorobenzoyl)amino]-3-(1H-indol-3-yl)propanoate
- Calcium (S)-3-methyl-2-oxovalerate
- Calcium 2,4-dichlorophenolate
- Calcium 2-ethylhexanoate
- Calcium 2-hydroxypropanoate
- Calcium 2-methoxyethoxide
- Calcium 2-oxoglutarate
- Calcium 3-methyl-2-oxovalerate