Electron microscopy studies of lutetium doped erbium silicide (Er0.9Lu0.1)5Si4
-
Add time:07/27/2019 Source:sciencedirect.com
Examination of bulk microstructures of lutetium doped erbium silicide (Er0.9Lu0.1)5Si4 (space group: Pnma) using scanning and transmission electron microscopy (SEM, TEM) reveals the existence of thin plates of a hexagonal phase (space group: P63/mcm) where the stoichiometric ratio in moles between the rare earths and Si is 5 to 3, i. e the 5:3 phase. The orientation relationship between the matrix and the plates was determined as [010]m ≈ ∥[-1010]p. This observation adds credence to the assumption that all linear features noted in alloys of the rare-earth intermetallic family R5(SixGe1-x)4 are of the stoichiometric ratio 5:3 and possess a common orientation relationship with the parent 5:4 alloys.
We also recommend Trading Suppliers and Manufacturers of LUTETIUM SILICIDE (cas 12032-13-2). Pls Click Website Link as below: cas 12032-13-2 suppliers
Prev:Initial stages of Lutetium growth on Si (111)-7 × 7 probed by STM and core-level photoelectron spectroscopy
Next:Thin films of rare earth metal silicides) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Preparation and crystal structure of quaternary silicide carbides with Dy2Fe2Si2C type structure08/03/2019
- Rare-earth silicide thin film study. Comparison of heavy ion and conventional RBS08/02/2019
- Standard enthalpies of formation of some lutetium alloys by high-temperature direct synthesis calorimetry08/01/2019
- Superconductivity of rare earth-iron silicides07/31/2019
- 57Fe Mössbauer study of Lu2Fe3Si5 iron silicide superconductor07/30/2019
- Preparation of yttrium silicides and oxide-silicides07/29/2019
- Thin films of rare earth metal silicides07/28/2019
- Initial stages of Lutetium growth on Si (111)-7 × 7 probed by STM and core-level photoelectron spectroscopy07/26/2019
-
Health and Chemical more >