Concentrated solar energy used for sintering MAGNESIUM TITANATE (cas 12032-30-3)s for electronic applications

Add time:07/28/2019    Source:sciencedirect.com

Solar energy is an important renewable source of energy with many advantages: it is unlimited, clean and free. The main objective of this work was to sinter magnesium titanate ceramics in a solar furnace using concentrated solar energy, which is a novel and original process. The direct conversion of solar power into high temperature makes this process simple, feasible and ecologically viable/environmentally sustainable. We performed the solar sintering experiments at Plataforma Solar de Almeria-CIEMAT, Spain. This process takes place in a vertical axis solar furnace (SF5–5 kW) hosting a mobile flat mirror heliostat, a fixed parabolic mirror concentrator, an attenuator and a test table the concentrator focus. We sintered (MgO)0.63(TiO2)0.37, (MgO)0.49(TiO2)0.51, (MgO)0.50(TiO2)0.50 ceramics samples in air at about 1100 °C for a duration of 16 min, 1 h, 2 h and 3 h in the solar furnace. The MgO/TiO2 ratio and the dwell time was varied in order to obtain phase pure MgTiO3 ceramic. We obtained a pure MgTiO3 geikielite phase by solar sintering of (MgO)0.63(TiO2)0.37 samples at 1100 °C (16 min–3 h). Samples of (MgO)0.63(TiO2)0.37, solar sintered at 1100 °C for 3 h, resulted in well-sintered, non-porous samples with good density (3.46 g/cm3). The sintered samples were analyzed by XRD for phase determination. The grain and surface morphology was observed using SEM. Electrical measurements were carried out on solar sintered samples. The effect of processing parameters on microstructure and dielectric properties were investigated and is presented.

We also recommend Trading Suppliers and Manufacturers of MAGNESIUM TITANATE (cas 12032-30-3). Pls Click Website Link as below: cas 12032-30-3 suppliers

Prev:Effect of MAGNESIUM TITANATE (cas 12032-30-3) content on microstructures, mechanical performances and dielectric properties of Si3N4-based composite ceramics
Next:Biodiesel production using a novel heterogeneous catalyst, MAGNESIUM ZIRCONATE (cas 12032-31-4) (Mg2Zr5O12): Process optimization through response surface methodology (RSM))