Magnetic and dielectric behavior of praseodymium substituted barium hexaferrite

Add time:07/30/2019    Source:sciencedirect.com

Magnetic and dielectric properties of barium hexaferrite doped with praseodymium at different calcination temperatures have been investigated. Sol gel auto-combustion method was used to synthesize Ba1-xPrxCoxFe12-xO19 (x = 0.4). Fourier-transform infrared spectroscopy (FTIR), thermo-gravimetry analysis (TGA), X-ray diffraction (XRD), transmission electron microscopy (TEM), vibrating sample magnetometer (VSM) and dielectric spectroscopy have been used to characterize the synthesized M-type hexaferrite. Analysis of FTIR, TGA and XRD results, confirmed the complete formation of M-type hexagonal phase with average crystallite size lying in the range 38 ± 5 nm. VSM analysis revealed the increase of coercivity, retentivity, and saturation magnetization at higher calcination temperature but under same condition decrease in the values of dielectric constant and tangent loss is observed by dielectric spectroscopy. On the basis of obtained results, Ba1- xPrxCoxFe12-xo19 (x = 0.4) calcinated at 800 °C is being proposed as a harder magnetic material for manufacturing permanent magnets.

We also recommend Trading Suppliers and Manufacturers of praseodymium dioxide (cas 12036-05-4). Pls Click Website Link as below: cas 12036-05-4 suppliers

Prev:Synthesis of ethane and ethylene from methane and carbon dioxide over praseodymium oxide catalysts
Next:The behaviour of praseodymium 4-hydroxycinnamate as an inhibitor for carbon dioxide corrosion and oxygen corrosion of steel in NaCl solutions)