Microstructure and oxidation performance of undoped and rhodium-doped aluminide coatings on Mar-M247 superalloy

Add time:07/26/2019    Source:sciencedirect.com

A rhodium modification of aluminide coating on Mar-M247 superalloy was performed by electrodepositing of 0.5 μm thick rhodium layer followed by chemical vapour aluminizing. It was found that rhodium dissolves in the aluminide coating. Oxidation resistance of undoped coating is worse than the rhodium-doped one (higher weight gain). The constant kp value confirms the favourable modification effect of rhodium on resistance against oxidation of aluminide coatings. Rhodium reduces the oxide growth rate three times. Moreover, it dissolves in the NiAl rather than in the γ′-Ni3Al during oxidation. The degradation rate from NiAl to γ′-Ni3Al and Al2O3 layer growth has decreased.

We also recommend Trading Suppliers and Manufacturers of Rhodium oxide (cas 12036-35-0). Pls Click Website Link as below: cas 12036-35-0 suppliers

Prev:Position and oxidation state of tin in Sn-bearing tetrahedrites Cu12-xSnxSb4S13
Next:Electrochromic properties of Rhodium oxide (cas 12036-35-0) thin films prepared by reactive sputtering under an O2 or H2O vapor atmosphere)