A novel ultra-high-temperature oxidation protective MoSi2-TaSi2 ceramic coating for tantalum substrate

Add time:07/28/2019    Source:sciencedirect.com

To protect refractory metal against oxidation at ultra-high temperatures, a MoSi2-TaSi2 ceramic coating was prepared on a pure tantalum (Ta) substrate using a novel three-step process, which included dip-coating with a molybdenum slurry, vacuum sintering, and halide-activated pack cementation (HAPC). The original coating had a MoSi2-TaSi2 double-layer structure from the surface to the substrate. After oxidation at 1700°C for 8 h in air, the coating exhibited a complex multi-layer structure composed of SiO2-Mo5Si3-MoSi2-(Mo,Ta)5Si3-TaSi2-Ta5Si3 from the outer layer to the inner layer, due to the high-temperature phase transition and diffusion of Si and O. The coating effectively protected the Ta substrate at 1700°C for 12 h without failure, thereby demonstrating great improvement to its service life in an ultra-high-temperature aerobic environment. The protective effect was attributed to the integrity of the ceramic coating and the formation of a dense, uniform SiO2 film that effectively lowered the inward oxygen diffusion rate.

We also recommend Trading Suppliers and Manufacturers of TANTALUM SILICIDE (cas 12039-79-1). Pls Click Website Link as below: cas 12039-79-1 suppliers

Prev:Photoluminescent properties of porous films of TANTALUM SILICIDE (cas 12039-79-1)s
Next:Microstructure and mechanical properties of tantalum carbide ceramics: Effects of Si3N4 as sintering aid)