Veining substructure in single-crystal Dimolybdenum carbide (cas 12058-19-4)

Add time:07/28/2019    Source:sciencedirect.com

Optical and electron microscopy on dimolybdenum carbide single crystals revealed a veining substructure on all planes of the as-grown crystals. Electron diffraction showed these veins to be hexagonal Mo2C, determined by chemical and electron microprobe analyses to be off-stoichiometric Mo2C0.97. Annealing in vacuum at 1600°–2000°C decreased the number of veins present. A substructure transition from veins to bands was observed after annealing at 2000°C, associated with γ'-MoC and Mo formation. Annealing at 2200°C or above caused the formation of bands found to be primarily Mo. The veining process is postulated to be due to a solidification and precipitation process. Polygonization of the veining substructure occurred during annealing below 2200°C. Room-temperature microhardness data on as-grown and annealed crystals further substantiated these findings.

We also recommend Trading Suppliers and Manufacturers of Dimolybdenum carbide (cas 12058-19-4). Pls Click Website Link as below: cas 12058-19-4 suppliers

Prev:Ultrafine WC-0.5Co-xTaC cemented carbides prepared by spark plasma sintering
Next:Liquid-exfoliated MOLYBDENUM TELLURIDE (cas 12058-20-7) nanosheets with superior electrocatalytic hydrogen evolution performances)