Characterization of microstructural stability for nanotwinned mercury cadmium telluride under cyclic nanoindentations
-
Add time:07/29/2019 Source:sciencedirect.com
Nanotwinned (nt) mercury cadmium telluride (HgCdTe or MCT) was prepared using nanoindentations. The hardness of nt-MCT is 100 times higher than that of monocrystalline counterparts. Transmission electron microscopy shows that the twin lamellae of nt-MCT prior to cyclic nanoindentations are distributed along two directions, intersecting at an angle of 76°. The nanotwinned microstructure of nt-MCT is stable after 100 cyclic nanoindentations. The loading–unloading curves of nt-MCT are basically invariable after 50 cycles, and have elastic characteristics.
We also recommend Trading Suppliers and Manufacturers of MERCURY (II) TELLURIDE (cas 12068-90-5). Pls Click Website Link as below: cas 12068-90-5 suppliers
Prev:Effect of annealing on the structural properties of arsenic-implanted mercury cadmium telluride
Next:Synthesis and characterization of mercury telluride nanoparticles using a new precursor) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Synthesis and characterization of nanocrystalline mercury telluride by sonochemical method08/05/2019
- Ultrahigh hardness and improved ductility for nanotwinned mercury cadmium telluride08/04/2019
- Scanning tunneling optical spectroscopy in mercury cadmium telluride and related compounds08/03/2019
- Formation of an emissive telluroxide promoted by Hg2+ in aqueous environment: A new naked-eye and ratiometric rhodamine dimer fluorescent mercury(II) probe08/02/2019
- An easy one-step procedure for the synthesis of novel β-functionalised tellurides08/01/2019
- 3-(Diphenylchalcogenophosphoryl)propionic acids as precursors for metal selenides and tellurides07/31/2019
- Synthesis and characterization of mercury telluride nanoparticles using a new precursor07/30/2019
- Effect of annealing on the structural properties of arsenic-implanted mercury cadmium telluride07/28/2019
-
Health and Chemical more >