Effects of adding YTTRIUM NITRATE (cas 10361-93-0) on the mechanical properties of hot-pressed AlN ceramics

Add time:08/02/2019    Source:sciencedirect.com

Aluminum nitride (AlN) ceramics were prepared by hot-pressing with Y(NO3)3·6H2O as sintering additive. The mechanical properties including flexural strength, Vickers’ hardness, and fracture toughness were studied. The relative density and mechanical property of the monolithic AlN were improved by adding Y(NO3)3·6H2O, which decreased the porosity. At 2 wt% Y2O3, the AlN ceramic exhibited the highest strength of 383 MPa, the highest hardness of 15.39 GPa, and the highest fracture toughness of 3.1 MPa m1/2. However, doping with more additive, the strength, hardness, and toughness of AlN ceramics decreased because of the weak interfacial bonding between AlN matrix and the yttrium aluminates phase.

We also recommend Trading Suppliers and Manufacturers of YTTRIUM NITRATE (cas 10361-93-0). Pls Click Website Link as below: cas 10361-93-0 suppliers

Prev:Effect of yttrium variation on phase, transparency, and micro-structure of neodymium doped yttrium aluminum garnet ceramic
Next:Exposure of hydrocarbon intumescent coatings to the UL1709 heating curve and furnace rheology: Effects of ZINC BORATE (cas 10361-94-1) on char properties)