Formation process of Akaganeite (cas 12134-57-5) in the simulated wet-dry cycles atmospheric environment
-
Add time:08/01/2019 Source:sciencedirect.com
In order to clarify the formation mechanism and conditions for Akaganeite (cas 12134-57-5) in long-term exposure, the influence of the former corrosion results on akaganeite formation was investigated by simulated experiments in laboratory. The combination of XRD, FTIR, SEM and EPMA enabled the identification of the rust layer formed on the surface. Accordingly, the nature of the rust layer and the amount of the corrosive species in the rust layer varied with the extension of the exposure. Among them, comparing with the corrosion condition in initial stage, the structure of rust layer after repeated wet-dry cycles was disadvantage for akaganeite formation. Element Cl aggregated at the interface between rust and substrate in the thick part can participate in the formation of akaganeite after the rust layer covered removed. The accumulation effect of salt deposited contributed to akaganeite formation under the condition that salt deposition rate was relatively low.
We also recommend Trading Suppliers and Manufacturers of Akaganeite (cas 12134-57-5). Pls Click Website Link as below: cas 12134-57-5 suppliers
Prev:Synthesis of Akaganeite (cas 12134-57-5) in the presence of sulfate: Implications for Akaganeite (cas 12134-57-5) formation in Yellowknife Bay, Gale Crater, Mars
Next:A novel Akaganeite (cas 12134-57-5) sorbent synthesised from waste red mud: Application for treatment of arsenate in aqueous solutions) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- A novel Akaganeite (cas 12134-57-5) sorbent synthesised from waste red mud: Application for treatment of arsenate in aqueous solutions08/02/2019
- Synthesis of Akaganeite (cas 12134-57-5) in the presence of sulfate: Implications for Akaganeite (cas 12134-57-5) formation in Yellowknife Bay, Gale Crater, Mars07/31/2019
- Synthesis and characterization of pure and Al-substituted Akaganeite (cas 12134-57-5)s and evaluation of their performance to adsorb As(V)07/30/2019