Structure, morphology and mechanism research on synthesizing XONOTLITE (cas 12141-77-4) fiber from acid-extracting residues of coal fly ash and carbide slag
-
Add time:08/02/2019 Source:sciencedirect.com
XONOTLITE (cas 12141-77-4) fibers have attracted much attention in super thermal insulation and flame retardant fields due to its ultra-light property. In this article, well crystalline xonotlite fibers were successfully prepared from two kinds of industry wastes, carbide slag and acid residues of fly ash respectively, by hydrothermal method. Influences of synthesis parameters, such as hydrothermal temperature, hydrothermal time and Ca:Si ratio, on both crystalline structure and micro morphology of hydrothermal products have been carefully researched. The results show that the formation of xonotlite fiber is remarkably accelerated by alumina impurities in carbide slag. Xonotlite phase could be formed within 24 h, and pure xonotlite fibers with satisfied crystalline degree are obtained after 48 h in this system. It also means that much thinner fibers could be achieved under a certain time. The resultant xonotlite fibers are in 50–300 nm diameter and 10–15 μm length. Moreover, because of relatively large particle size of carbide slag, pectolite intermediate is generated due to the temporary deficient condition of free calcium species. Furthermore, the phase type of product could be effectively controlled by altering Ca:Si ratio under suitable hydrothermal system. And xonotlite phase could be obtained under a wide range of Ca:Si ratio.
We also recommend Trading Suppliers and Manufacturers of XONOTLITE (cas 12141-77-4). Pls Click Website Link as below: cas 12141-77-4 suppliers
Prev:Effect of Ultrasonic Process on Carbide Slag Activity and Synthesized XONOTLITE (cas 12141-77-4)
Next:Phosphate removal and recovery through crystallization of hydroxyapatite using XONOTLITE (cas 12141-77-4) as seed crystal) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Thermal conductivity measurements on XONOTLITE (cas 12141-77-4)-type calcium silicate by the transient hot-strip method08/08/2019
- Removal of organic polyelectrolytes and their metal complexes by adsorption onto XONOTLITE (cas 12141-77-4)08/07/2019
- Mechanisms of Nd(III) uptake by 11 Å tobermorite and XONOTLITE (cas 12141-77-4)08/06/2019
- Structure of the hydrogen bonds and silica defects in the tetrahedral double chain of XONOTLITE (cas 12141-77-4)08/05/2019
- Inverse relation between the catalytic activity and catalyst concentration for the ruthenium(0) nanoparticles supported on XONOTLITE (cas 12141-77-4) nanowire in hydrogen generation from the hydrolysis of sodium borohydride08/04/2019
- Phosphate removal and recovery through crystallization of hydroxyapatite using XONOTLITE (cas 12141-77-4) as seed crystal08/03/2019
- Effect of Ultrasonic Process on Carbide Slag Activity and Synthesized XONOTLITE (cas 12141-77-4)08/01/2019
- Hydrothermal synthesis of XONOTLITE (cas 12141-77-4) from carbide slag07/31/2019
- Fabrication and characterization of form-stable phase change material/XONOTLITE (cas 12141-77-4) microcomposites07/30/2019