An approach to developing enhanced dielectric property nanocomposites based on acrylate elastomer

Add time:08/06/2019    Source:sciencedirect.com

High dielectric constant (high-k) polymeric materials suitable for electromechanical transducers should meet the requirements of low dielectric loss. This work introduced a ternary nanocomposite with acrylate elastomer (AE) as matrix, and chemically reduced graphene oxides (G) and poly(ionic liquid)s (PILs) as co-filler, of which AE was synthesized by solution polymerization. A unique hybrid (H) was fabricated by the ionic liquid monomers polymerized on the surface of graphene. Afterwards, hybrid of different filler contents was added into AE to prepare nanocomposites with solution casting method. The favorable π-π interaction between PILs and graphene made the co-filler a better dispersion in the matrix, which contributed to the enhanced dielectric property of the resultant nanocomposites. Dielectric constant of H/AE nanocomposite at 102 Hz was as high as 680 and the dielectric loss was only 0.34 when the filler content (1.69 vol%) approached to the percolation threshold (fc), which was attributed to PILs anchored on the surface of graphene acting as spacers and PILs cut the leakage currents induced by the direct connection of graphene. Moreover, the composite was still flexible that could engender larger strain in area.

We also recommend Trading Suppliers and Manufacturers of DISPERSE RED 13 ACRYLATE 98 (cas 10462-94-9). Pls Click Website Link as below: cas 10462-94-9 suppliers

Prev:RAFT copolymerization of amphiphilic poly (ethyl acrylate-b-acrylic acid) as wetting and dispersing agents for water borne coating
Next:Enantiomeric separations of halogen-substituted 2-aryloxypropionic acids by high-performance liquid chromatography on a terguride-based chiral stationary phase)