Structural studies of novel di-ureasil ormolytes doped with lithium hexafluoroantimonate

Add time:08/03/2019    Source:sciencedirect.com

Hybrid electrolytes produced by the sol–gel process were obtained by doping a di-urea cross-linked POE/siloxane hybrid host framework (d-U(2000)) with lithium hexafluoroantimonate (LiSbF6). Flexible, transparent xerogel films with ∞ > n ≥ 2.5 (where n, composition, represents the molar ratio of oxyethylene units OCH2CH2 per Li+ ion), thermally stable to at least 200 °C, were prepared. At 30 °C the highest ionic conductivity of all the electrolytes prepared was 1.32 × 10− 5 S cm− 1 for n = 30. The electrochemical stability windows of these materials span at least 6.0 V. Samples with n < 200 are amorphous, homogeneous and non-porous. Crystallites of POE are formed in the most dilute electrolyte (n = 200). The guest Li+ ions were shown to coordinate to the oxygen atoms of the urea carbonyl groups over the entire range of salt concentration. The great majority of the SbF6− ions interact with the Li+ ions. Contact ion pairs were detected only at n = 200. Trace amounts of “free” anions exist in all electrolyte samples.

We also recommend Trading Suppliers and Manufacturers of POTASSIUM HEXAFLUOROANTIMONATE (cas 16893-92-8). Pls Click Website Link as below: cas 16893-92-8 suppliers

Prev:The heat capacity of POTASSIUM HEXAFLUOROANTIMONATE (cas 16893-92-8)(V) from 21 to 284 K
Next:Gravimetric and spectrophotometric determination of hexafluoroantimonate with tetraphenylarsonium chloride, nitron and ferroin)