Enhancement of isobutane refrigerator performance by using far-infrared coating

Add time:08/08/2019    Source:sciencedirect.com

This study evaluated the effect on refrigeration performance and feasibility of a far-infrared coating (FIRC) on the condenser of a small isobutane (R-600a) refrigerator. The evaluation was based on the no-load pull-down and 24-h on-load cycling tests. Far-infrared materials and a water-based coating material were mixed using a two-step synthesis method to obtain the FIRC material. Fourier transform infrared spectrometry established that the optimal far-infrared material was a multiwalled carbon nanotube (MWCNT). The results of the no-load pull-down test revealed that the electricity consumption, freezer temperature, and coefficient of performance (COP) of the R-600a refrigerator with MWCNT-FIRC (S2) were lower than those of the refrigerator without MWCNT-FIRC (S1) by 3.39%, 3.61%, and 2.92%, respectively. The results of the 24-h on-load cycling test showed that S2 had a lower electricity consumption, higher slope of pull-down (SPD), higher compression ratio (CR), higher COP, lower duty ratio (DR), and higher energy factor (EF), changing upon those of S1 by −7.05%, 5.66%, 3.24%, 5.92%, −5.63, and 7.89%, respectively. A MWCNT-FIRC on the condenser of an R-600a refrigerator can enhance refrigeration performance and reduce electricity consumption, resulting in energy saving and carbon reduction.

We also recommend Trading Suppliers and Manufacturers of Disperse Red B-BL (cas 12223-42-6). Pls Click Website Link as below: cas 12223-42-6 suppliers

Prev:An efficient ordered mesoporous molybdate-zirconium oxophosphate solid acid catalyst with homogeneously dispersed active sites: Synthesis, characterization and application
Next:Dispersive micro solid-phase extraction (DµSPE) with graphene oxide as adsorbent for sensitive elemental analysis of aqueous samples by laser induced breakdown spectroscopy (LIBS))