Structural evolution of calcium-exchanged (NH4)2SiF6-dealuminated Y zeolite after various chemical treatments

Add time:08/07/2019    Source:sciencedirect.com

The structural evolution of Y zeolite (Si/Al 2.17) weakly dealuminated by hexafluorosilicate (Si/Al 3.13), denoted YD, and exchanged with calcium (CaYD), has been studied after acid–base treatments at 80 °C close to the cation exchange conditions. The stability of the samples was followed by X-ray diffraction and solid-state NMR of 29Si and 27Al; YD zeolite was completely destroyed by treatment with acid pH 2.5 and suffered serious degradation on treatment with alkali at pH 11.8. The introduction of calcium improved the stability of the zeolite in acid and base. In acid CaYD was not destroyed until pH 1. At pH 2, silicon and aluminium were extracted and an amorphous phase was formed. Base treatment at pH 13 did not affect the calcium-exchanged zeolite.

We also recommend Trading Suppliers and Manufacturers of Calcium hexafluorosilicate (cas 16925-39-6). Pls Click Website Link as below: cas 16925-39-6 suppliers

Prev:Leaching and recovery of phosphate and rare earth elements from an iron-rich fluorapatite concentrate: Part II: Selective leaching of calcium and phosphate and acid baking of the residue
Next:Structural evolution of calcium or lanthanum-exchanged (NH4)2SiF6-dealuminated y zeolite after various chemical treatments)