Effect of hydration temperature on the structure reconstruction of MgAlY layered materials

Add time:08/12/2019    Source:sciencedirect.com

This contribution investigates the obtaining of layered double hydroxides (LDHs) modified with different concentrations of yttrium and the effect of the yttrium concentration and temperature during the rehydration of the mixed oxides derived from these solids. Mg3Al(1−x)Yx-LDH (where x = 0.04–0.6) have been prepared using the standard coprecipitation method under low supersaturation conditions. After the calcination of these solids (460 °C, 18 h), the corresponding mixed oxides were obtained. The reconstruction of the layered structure was attempted by rehydration of the mixed oxides under two different conditions: (1) at 25 °C and (2) at 70 °C. All the aforementioned solids have been characterized by chemical analysis, X-ray diffraction, DRIFTS spectra, N2 adsorption–desorption isotherms, and determination of base sites. Their catalytic activity was tested in cyanoethylation of ethanol with acrylonitrile. The results obtained after the characterization and the catalytic activity tests were compared with those obtained for a standard hydrotalcite Mg3Al.

We also recommend Trading Suppliers and Manufacturers of YTTRIUM NITRATE HYDRATE (cas 13470-40-1). Pls Click Website Link as below: cas 13470-40-1 suppliers

Prev:Structurally diverse dysprosium and yttrium complexes containing an amine-bis(benzotriazole phenolate) ligand: Synthesis, characterization and catalysis for lactide polymerization
Next:Boronic ester-linked macrocyclic lipopeptides as serine protease inhibitors targeting Escherichia coli type I signal peptidase)