Fabrication of α-alumina fibers by sol-gel and electrospinning of Aluminum nitrate (cas 13473-90-0) precursor solutions

Add time:08/05/2019    Source:sciencedirect.com

The fabrication of dense alumina fibers at low cost by sol-gel and electrospinning, using Aluminum nitrate (cas 13473-90-0) as precursor is reported. Polyvinyl pyrrolidone was used as spinning polymer, while Pluronic 127 was used as additive to achieve a porous structure. The material was characterized at different stages of thermal treatment by SEM, EDS, FTIR, XRD, and thermal analyses. It was observed that the increase in precursor ratio is related to the formation of more stable fibers that retain their morphology after sintering at 1600 °C. The fibers obtained from a solution with high mole ratio presented a mean diameter close to nanometric scale 153 ± 39 nm. FTIR and XRD demonstrated that amorphous, γ-, and δ-Al2O3 polymorphs were present in fibers treated at 800 °C, while α-Al2O3 was formed in samples at approximately 1000 °C. EDS and XRD study demonstrated the high purity and crystalline form of the alumina fibers.

We also recommend Trading Suppliers and Manufacturers of Aluminum nitrate (cas 13473-90-0). Pls Click Website Link as below: cas 13473-90-0 suppliers

Prev:Synthesis and optical properties of powders of lutetium and yttrium double phosphates-doped by ytterbium
Next:Can nonalcoholic beer, silicon and hops reduce the brain damage and behavioral changes induced by Aluminum nitrate (cas 13473-90-0) in young male Wistar rats?)