Effect of Ni addition on pressureless sintering of tungsten diboride (cas 12228-69-2)

Add time:08/08/2019    Source:sciencedirect.com

WB2 ceramic was prepared by a two-step-sintering method. First, phase-pure WB2 powder was successfully synthesised by solid-state reaction using tungsten and boron powder with a molar ratio of 1:2.5. The mixed powders were treated by pressureless high-temperature synthesis (1500 °C, 1 h, in vacuum). Second, WB2 powder with Ni was used as a sintering aid (1500 °C, 1 h, in vacuum), and the influence of the content of sintering aids on the density, porosity, phase and microstructure was studied. The relationship between Vickers micro-hardness, flexural strength and microstructure was also investigated. The result showed that the properties of the WB2 ceramic can be optimised by adjusting the content of sintering aids. The best performance of the WB2 ceramic is obtained using a sintering aid content of 5 wt.%; the relative density, porosity, Vickers micro-hardness and flexural strength of the sintered sample can reach 91.80%, 3.30%, 2623 MPa and 170 MPa, respectively.

We also recommend Trading Suppliers and Manufacturers of tungsten diboride (cas 12228-69-2). Pls Click Website Link as below: cas 12228-69-2 suppliers

Prev:Friction and wear properties of zirconium diboride in sliding against WC ball
Next:Analysis of pressureless sintering of titanium diboride ceramics with nickel, cobalt, and tungsten carbide additives)