Ohmic contacts simultaneously formed on n-type and p-type 4H-SiC at low temperature

Add time:08/16/2019    Source:sciencedirect.com

The properties of 4H–SiC/Ni/Ti/Al/W metal contacts on n-type and p-type ion-implanted 4H–SiC layers are studied in this paper, with the aim of realizing simultaneous ohmic contact formation. The thickness of the Al film and the alloying temperature are analyzed. Specific contact resistances of 8 × 10−4 Ω cm2 and 4.1 × 10−5 Ω cm2 were achieved with multi-metal layer Ni/Ti/Al/W (80/30/110/50 nm) for n-type and p-type 4H–SiC, respectively, at an annealing temperature of 750 °C. This is for first time at such a low annealing temperature that ohmic contacts have been reported to simultaneously form on n-type and p-type 4H–SiC with satisfactory specific contact resistances. Samples were characterized using AFM, XRD, AES and TEM, and the results indicate that the presence of the W top layer facilitates lowering the surface roughness and accumulating elemental Ni and Al on the SiC side during annealing, which benefits the formation of the ohmic contacts.

We also recommend Trading Suppliers and Manufacturers of 5(4H)-Thiazolethione (cas 106986-37-2). Pls Click Website Link as below: cas 106986-37-2 suppliers

Prev:Molecular docking, dynamics simulations and 3D-QSAR modeling of arylpiperazine derivatives of 3,5-dioxo-(2H,4H)-1,2,4-triazine as 5-HT1AR agonists
Next:Synthesis and biological evaluation of new 9-aminoacridine-4-carboxamide (cas 106988-43-6) derivatives as anticancer agents)