Preparation of CHABAZITE (cas 12251-32-0) with mesopores templated from a cationic polymer
-
Add time:08/10/2019 Source:sciencedirect.com
Mesoporous CHABAZITE (cas 12251-32-0) zeolites were prepared by using the cationic polymer polydiallyldimethylammonium chloride (PDADMAC) as template for mesopores and N,N,N-trimethyl-1-adamantammonium hydroxide as structure directing agent for the chabazite framework. The prepared zeolites had large surface areas and significant mesopore volumes that increased with high PDADMAC loading. Nitrogen sorption isotherms of chabazite zeolites with low loadings of PDADMAC (0.8–2.3 wt.%) displayed a composite of Type I and II with a broad H4 hysteresis loop at p/po=0.8–1.0. At a high polymer loading (3.1 wt.%) the resulting zeolite displayed the Type IV sorption isotherm and H3 hysteresis. The chabazite zeolites prepared with 0.8–2.3 wt.% polymer had exponentially decaying mesopore size distribution curves ranging from 2 to 30 nm centred around 4–5 nm. A polymer loading of 3.1 wt.% gave a zeolite with a multimodal meso- and macropore size distribution curve ranging from 2 to 140 nm. Adjusting the synthesis gel composition made it possible to prepare mesoporous chabazite zeolites with PDADMAC loadings up to 3.1 wt.% at Si/Al = 20–70.
We also recommend Trading Suppliers and Manufacturers of CHABAZITE (cas 12251-32-0). Pls Click Website Link as below: cas 12251-32-0 suppliers
Prev:Seeded growth of isomorphously substituted CHABAZITE (cas 12251-32-0)s in proton-form
Next:Hydrogen (H2) adsorption on natural and cation-exchanged clinoptilolite, mordenite and CHABAZITE (cas 12251-32-0)) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- TiO2-CHABAZITE (cas 12251-32-0) semiconductor composites for photocatalytic degradation of rhodamine under sunlight irradiation08/17/2019
- Photodecolorization of rhodamine under sunlight irradiation driven by CHABAZITE (cas 12251-32-0)08/16/2019
- Understanding the AC conductivity and permittivity of trapdoor CHABAZITE (cas 12251-32-0)s for future development of next-generation gas sensors08/15/2019
- Preparation of CHA zeolite (CHABAZITE (cas 12251-32-0)) crystals and membranes without organic structural directing agents for CO2 separation08/14/2019
- Effect of core-shell structuring of CHABAZITE (cas 12251-32-0) zeolite with a siliceous zeolite thin layer on the separation of acetone-butanol-ethanol vapor in humid vapor conditions08/13/2019
- Differential penetration of ethanol and water in Si-CHABAZITE (cas 12251-32-0): High pressure dehydration of azeotrope solution08/12/2019
- Hydrogen (H2) adsorption on natural and cation-exchanged clinoptilolite, mordenite and CHABAZITE (cas 12251-32-0)08/11/2019
- Seeded growth of isomorphously substituted CHABAZITE (cas 12251-32-0)s in proton-form08/09/2019
- Impact of surface modification of CHABAZITE (cas 12251-32-0) on the sorption of iodine and molybdenum radioisotopes from liquid phase08/08/2019