Facile synthesis of mesoporous Fe-based MOFs loading bismuth with high speed adsorption of iodide from solution

Add time:08/09/2019    Source:sciencedirect.com

To improve the uptake effect of iodide anions from aqueous solution, mesoporous Fe-based MOFs ([email protected]) were prepared by mixing Bi(III) and MIL-101(Fe) in Teflon-lined autoclave using solvothermal synthetic method. The [email protected] adsorbents were characterized by IR, XRD, SEM, BET and XPS, indicating the crystal structure of MIL-101(Fe) remained when the addition of Bi(III) species in the synthesis of [email protected] was below 5.0%. When the amount of Bi(III) reached 15.0%, mesoporous Fe-based MOFs was obtained. [email protected] composites displayed fast adsorption kinetics and the adsorption equilibrium was achieved in 20 min in 200 mg L−1 of iodide anions solution concentration at neutral medium. The pH of solution could affect adsorption of iodide anions and the maximum adsorption capacities occurred at pH 3.

We also recommend Trading Suppliers and Manufacturers of bismuth iodide (cas 12262-07-6). Pls Click Website Link as below: cas 12262-07-6 suppliers

Prev:A photosensor based on lead-free perovskite-like methyl-ammonium bismuth iodide (cas 12262-07-6)
Next:Electric field assisted spray coated lead free bismuth iodide (cas 12262-07-6) perovskite thin film for solar cell application)