PVC and AGALMATOLITE (cas 12284-46-7) composite characterization

Add time:08/09/2019    Source:sciencedirect.com

The purpose of this work was to characterize PVC and AGALMATOLITE (cas 12284-46-7) composites and to evaluate the effects of this mineral filler through thermal analysis and mechanical property measurements. The glass transition temperature, as well as some mechanical properties, were evaluated through comparative analysis with respect to PVC and calcium carbonate composites, prepared with the same composition and operating conditions.DSC results show that there is a slight decrease in the glass transition temperature of the composites as agalmatolite content increases from 10 to 40 phr. The same does not occur with composites prepared using calcium carbonate, which practically do not show any difference in the same filler content range. Among the mechanical properties evaluated at ambient temperature (25°C), Young's modulus and elongation at break of the composites made with agalmatolite are slightly higher than those using calcium carbonate, thus the resistance to elastic deformation and plasticity of the composites may be enhanced when agalmatolite is used as the mineral filler in PVC composites.

We also recommend Trading Suppliers and Manufacturers of AGALMATOLITE (cas 12284-46-7). Pls Click Website Link as below: cas 12284-46-7 suppliers

Prev:Direct wiring of the AZURIN (cas 12284-43-4) redox center to gold electrodes investigated by protein film voltammetry
Next:BAKUCHIOL (cas 17015-60-0) suppresses oestrogen/testosterone-induced Benign Prostatic Hyperplasia development through up-regulation of epithelial estrogen receptor β and down-regulation of stromal aromatase)