Photocatalytic degradation of gaseous trichloroethylene on porous titanium dioxide pellets modified with copper(II) under visible light irradiation

Add time:08/14/2019    Source:sciencedirect.com

Porous titanium dioxide pellets modified with copper(II) ion (Cu-TiO2) were synthesized by sol-gel method with dialysis for photocatalytic degradation of gaseous trichloroethylene (TCE) under visible light (VL) irradiation. TCE was completely degraded by passing the gas stream (mole fractions of oxygen and TCE were 0.2 and 1.75 × 10−4, respectively) at the flow rate of 25 mL min−1 through 0.2 g of the Cu-TiO2 pellets (Cu content: 0.1 atom%) calcined at 200 °C. TCE was converted mainly to carbon dioxide, dichloroacetic acid (DCAA), and inorganic chlorine species. Relatively small quantities of pentachloroethane (PCA) and trichloroacetaldehyde (TCAH) were detected as products on the Cu-TiO2 surface. Comparison with porous TiO2 pellets under ultraviolet irradiation revealed that more chlorinated products and less carbon dioxide were formed on Cu-TiO2 under VL irradiation. The mineralization of TCE to carbon dioxide was calculated to be only ca. 30.0%. It is noted that DCAA, PCA and TCAH were accumulated on the surface and were extracted with ethyl acetate. The porous Cu-TiO2 pellets show promise as the photocatalyst acting under VL irradiation for converting TCE gas to chlorinated compounds which can be used in industries.

We also recommend Trading Suppliers and Manufacturers of TITANIUM(IV) NITRATE 99.9+% (cas 12372-56-4). Pls Click Website Link as below: cas 12372-56-4 suppliers

Prev:Degradation of bromate by Fe(II)Ti(IV) layered double hydroxides nanoparticles under ultraviolet light
Next:Stoichiometric relation for extraction of zirconium and hafnium from acidic nitrate solutions with Cyanex272)