Fabrication and characterization of porous cordierite (cas 1302-88-1) ceramics prepared from fly ash and natural minerals

Add time:08/15/2019    Source:sciencedirect.com

Low cost, single-phase porous cordierite (cas 1302-88-1) ceramics are successfully synthesized by in-situ solid-state reactions from fly ash, quartz, and magnesite. The effects of sintering temperature and magnesite content on phase transformation, open porosity, bulk density, mechanical properties, and microstructure are carefully investigated. Factsage analyses are carried out to calculate the isopleth diagrams, and the results agree well with the experimental outcomes. Thermal gravimetric and differential scanning calorimeter analyses (TG-DSC) are performed to characterize the weight loss and transient behaviors of the raw materials. Linear thermal expansion properties are also studied. The α-cordierite phase is the only phase observed in S-3 (magnesite content 25%) sintered at 1300 °C for 2 h, and its linear thermal expansion coefficient (2.71 × 10−6 K−1) is close to that of typical cordierite. Both the compressive strength (72.64 MPa) and flexural strength (23.92 MPa) of the as-synthesized samples are high with an open porosity of 33.16% and a bulk density of 1.61 g/cm3.

We also recommend Trading Suppliers and Manufacturers of cordierite (cas 1302-88-1). Pls Click Website Link as below: cas 1302-88-1 suppliers

Prev:Influence of dispersing agents on microstructure-related properties of slip cast cordierite (cas 1302-88-1) ceramics
Next:Development of porous MULLITE (cas 1302-93-8) and MULLITE (cas 1302-93-8)-Al2O3 composite for microfiltration membrane applications)