Influence of potassium hydroxide pretreatment on the extraction of gold and silver from a refractory ore

Add time:08/17/2019    Source:sciencedirect.com

Potassium hydroxide alkaline pretreatment of a refractory gold–silver ore containing 20 g/t Au and 220 g/t Ag was investigated with the purpose to evaluate its effectiveness on the extraction of gold and silver. The presence of antimony minerals such as stibnite (Sb2S3), zinkenite (Pb9Sb22S42) and andorite (Sb3PbAgS6) is the main reason for the refractory nature of the ore. Silver occurs as andorite, a Au–Ag alloy, tetrahedrite [(Cu,Fe,Zn,Ag)12Sb4S13] and in minor amounts in zinkenite whereas gold is associated with quartz and the antimony minerals. Cyanidation tests of the as-received ore show that the extraction of gold and silver is consistently low (i.e. ≤ 49.3% and ≤ 18.7%, respectively) over the leaching period of 24 h. The effects of potassium hydroxide concentrations (0.5–5 mol/L), temperature (20–80 °C) and particle size (5–50 μm) on the removal efficiency of antimony were investigated. Accompanying the removal of antimony, gold and silver recoveries improved with increases in the KOH concentrations (5 mol/L) and temperature (80 °C), and a decrease in the particle size (5 μm). Gold and silver extractions during subsequent cyanidation were improved to 87.6% and 94.5%, respectively, corresponding to 85.5% Sb removal by alkaline pretreatment. The antimony removal is also evidenced by the disappearance of stibnite, zinkenite and andorite which formed 4.57 wt.% of the original ore. The residual amount of antimony is due to the presence of unreactive Sb oxide and Pb–Sb sulphate minerals, sphalerite and tetrahedrite in the ore and Sb-bearing Pb sulphate compound(s) that formed during pretreatment. These findings indicate that potassium alkaline leaching can be an effective pretreatment method for refractory antimonial gold–silver ores.

We also recommend Trading Suppliers and Manufacturers of Gold hydroxide (cas 1303-52-2). Pls Click Website Link as below: cas 1303-52-2 suppliers

Prev:Mono-and co-applications of Ca-bentonite with zeolite, Ca-hydroxide, and tobacco biochar affect phytoavailability and uptake of copper and lead in a gold mine-polluted soil
Next:The hybrid of gold nanoparticles and Ni(OH)2 nanosheet for non-enzymatic glucose sensing in food)