The effect of heat-treatment on the structural characteristics of nanocrystalline chlorapatite (cas 1306-04-3) particles synthesized via an in situ wet-chemical route

Add time:08/15/2019    Source:sciencedirect.com

In this research, nanocrystalline chlorapatite (cas 1306-04-3) particles were synthesized via an in situ wet-chemical precipitation method at room temperature, and then various heat-treatment temperatures were examined to consider the effect of the heat-treatment process on the structure and morphology of the samples. According to the XRD results, by increasing the heat-treatment temperature, no phase transformation occurred, and all the samples were made of chlorapatite. However, the morphology of the nanoparticles changed from spherical to polygonal and grain growth occurred slowly. In addition, the Williamson–hall plot showed that the crystallite size before and after calcination at 500, 900, and 1200 °C was 13, 11, 20, and 34 nm, respectively, and a gradual increase in the crystallite size of chlorapatite was observed with increasing in the heat-treatment temperature.

We also recommend Trading Suppliers and Manufacturers of chlorapatite (cas 1306-04-3). Pls Click Website Link as below: cas 1306-04-3 suppliers

Prev:Nanoscale conversion of chlorapatite (cas 1306-04-3) into hydroxyapatite using ultrasound irradiation
Next:Synthesis and application of magnetic chlorapatite (cas 1306-04-3) nanoparticles for zinc (II), cadmium (II) and lead (II) removal from water solutions)